TY - GEN A1 - Obstarczyk, Agata A1 - Kaczmarek, Danuta A1 - Wojcieszak, Damian A1 - Mazur, Michał A1 - Domaradzki, Jarosław A1 - Kotwica, Tomasz A1 - Pastuszek, Roman A1 - Schmeißer, Dieter A1 - Mazur, Piotr A1 - Kot, Małgorzata T1 - Tailoring optical and electrical properties of thin-film coatings based on mixed Hf and Ti oxides for optoelectronic application T2 - Materials and Design N2 - In this work multi-magnetron sputtering stand was used for the deposition of the mixed oxides thin films based on HfO2 and TiO2. In order to obtain various material composition the power released to each magnetron (containing metallic hafnium and titanium targets) was precisely selected. Structural, surface, optical, electrical and mechanical properties of as-deposited coatings were analyzed. Depending on the hafnium content in the deposited thin films various types of the microstructure was obtained, i.e. HfO2-monoclinic, amorphous and TiO2-rutile. Increase of Ti content above 28 at. % in the as-prepared mixed oxides coatings caused their amorphization. It was found that with an increase of Ti content in prepared coatings their surface roughness and simultaneously water contact angle decreased. Performed measurements of electrical properties revealed that the lowest leakage current density in the range of 10−7 – 10−8 A/cm2 was obtained for amorphous coatings. Moreover, the tailoring of the dielectric constant was possible by a proper selection of material composition and microstructure of the deposited thin films. Average transparency in the visible wavelength region was in the range of ca. 79–86%. The influence of material composition and structure on shifting of the fundamental absorption edge and optical bandgap energy was also observed. The refractive index increased with an increase of Ti content, while extinction coefficient was the lowest for amorphous coatings. Additionally, hardness values were dependent on the material composition and optical packing density and were in the range from 7.6 GPa to 10.1 GPa. KW - Magnetron sputtering KW - Optical coatings KW - Electrical properties KW - Mixed oxides KW - HfO2 KW - TiO2 KW - High-k oxides KW - Amorphous thin films Y1 - 2019 U6 - https://doi.org/10.1016/j.matdes.2019.107822 SN - 0264-1275 VL - 175 ER - TY - GEN A1 - Kapuścik, Paulina A1 - Wojcieszak, Damian A1 - Pokora, Patrycja A1 - Mańkowska, Ewa A1 - Domaradzki, Jarosław A1 - Mazur, Michał A1 - Mazur, Piotr A1 - Kosto, Yuliia A1 - Morales, Carlos A1 - Kot, Małgorzata A1 - Flege, Jan Ingo T1 - Low temperature hydrogen sensor with high sensitivity based on CeOx thin film T2 - Sensors and Actuators B: Chemical N2 - In this work, a 500 nm-thick cerium oxide thin film was prepared by electron beam evaporation. It was found that the deposition of 7 nm thick Pd catalyst was required for obtaining a sensor response to hydrogen. The Pd/CeOx sensing structure has a high response of 5000 towards 25 ppm H2 at a working temperature of 200 °C and exhibits a sensor response of 1.3 at temperatures near ambient. Furthermore, the sensing structure exhibited excellent response/recovery kinetics. The results confirm that the CeOx-based materials are a promising material for the fabrication of room-temperature hydrogen sensors. KW - Cerium oxide KW - Thin film KW - Hydrogen sensing KW - Low operating temperature Y1 - 2024 U6 - https://doi.org/10.1016/j.snb.2024.136148 SN - 0925-4005 VL - 417 PB - Elsevier BV ER - TY - GEN A1 - Morales, Carlos A1 - Tschammer, Rudi A1 - Pożarowska, Emilia A1 - Kosto, Julia A1 - Villar‐Garcia, Ignacio J. A1 - Pérez‐Dieste, Virginia A1 - Favaro, Marco A1 - Starr, David E. A1 - Kapuścik, Paulina A1 - Mazur, Michał A1 - Wojcieszak, Damian A1 - Domaradzki, Jarosław A1 - Alvarado, Carlos A1 - Wenger, Christian A1 - Henkel, Karsten A1 - Flege, Jan Ingo T1 - Hydrogen sensing via heterolytic H₂ activation at room temperature by atomic layer deposited ceria T2 - ChemSusChem : chemistry, sustainability, energy, materials N2 - Ultrathin atomic layer deposited ceria films (<20 nm) are capable of H2 heterolytic activation at room temperature, undergoing a significant reduction regardless of the absolute pressure, as measured under in‐situ conditions by near ambient pressure X‐ray photoelectron spectroscopy. ALD‐ceria can gradually reduce as a function of H2 concentration under H2/O2 environments, especially for diluted mixtures below 10 %. At room temperature, this reduction is limited to the surface region, where the hydroxylation of the ceria surface induces a charge transfer towards the ceria matrix, reducing Ce4+ cations to Ce3+. Thus, ALD‐ceria replicates the expected sensing mechanism of metal oxides at low temperatures without using any noble metal decorating the oxide surface to enhance H2 dissociation. The intrinsic defects of the ALD deposit seem to play a crucial role since the post‐annealing process capable of healing these defects leads to decreased film reactivity. The sensing behavior was successfully demonstrated in sensor test structures by resistance changes towards low concentrations of H2 at low operating temperatures without using noble metals. These promising results call for combining ALD‐ceria with more conductive metal oxides, taking advantage of the charge transfer at the interface and thus modifying the depletion layer formed at the heterojunction. KW - Atomic Layer Deposition KW - Ceria KW - Hydrogen Sensing KW - X-Ray photoelectron spectroscopy KW - Raman spectroscopy KW - Resitive sensor Y1 - 2025 U6 - https://doi.org/10.1002/cssc.202402342 SN - 1864-5631 VL - 18 IS - 13 SP - 1 EP - 13 PB - Wiley-VCH CY - Weinheim ER -