TY - CHAP A1 - Henkel, Karsten A1 - Kot, Małgorzata A1 - Richter, Matthias A1 - Tallarida, Massimo A1 - Schmeißer, Dieter ED - Wandelt, Klaus T1 - An (In Situ)² Approach: ALD and resPES Applied to Al₂O₃, HfO₂, and TiO₂ Ultrathin Films T2 - Encyclopedia of Interfacial Chemistry: Surface Science and Electrochemistry, Vol. 3.1 N2 - Oxide surface coatings are of importance in tailoring interface properties with respect to surface passivation, adjustment of surface potentials, or providing active centers for surface reactions. In this contribution, we report about surface coatings prepared by the atomic layer deposition (ALD) method. ALD is known for its conformal growth of ultrathin, dense films which exhibit a low concentration of pinholes. KW - Atomic layer deposition (ALD) KW - Resonant photoelectron spectroscopy (resPES) KW - Band scheme KW - Partial density of states (pDOS) KW - Intrinsic charges KW - Intrinsic defects KW - Aluminum oxide (Al₂O₃) KW - Hafnium oxide (HfO₂) KW - Titanium oxide(TiO₂) Y1 - 2018 SN - 978-0-12-809739-7 SN - 978-0-12-809894-3 U6 - https://doi.org/10.1016/B978-0-12-409547-2.13852-1 SP - 18 EP - 26 PB - Elsevier CY - Oxford ER - TY - CHAP A1 - Schmeißer, Dieter A1 - Kot, Małgorzata A1 - Corrêa, Silma Alberton A1 - Das, Chittaranjan A1 - Henkel, Karsten ED - Wandelt, Klaus T1 - Interface Potentials, Intrinsic Defects, and Passivation Mechanisms in Al₂O₃, HfO₂, and TiO₂ Ultrathin Films T2 - Encyclopedia of Interfacial Chemistry: Surface Science and Electrochemistry, vol. 3.1 N2 - We study the electronic structure of ultrathin Al₂O₃, HfO₂, and TiO₂ ALD films by resonant photoelectron spectroscopy. We identify intrinsic defects which are responsible for the active sites in interface reactions, for the incorporation of intrinsic charges, and for the formation of local dipole momenta. All of these features determine the surface potentials and the reactivity of the surface of the atomic layer deposition coated systems. We give examples of charges and dipoles in Al₂O₃, on a study of the surface potentials in HfO₂, and relate the intrinsic defects in TiO₂ to their electrochemical relevance. KW - Atomic layer deposition (ALD) KW - Resonant photoelectron spectroscopy (resPES) KW - Band scheme KW - Interface potential KW - Intrinsic charges KW - Intrinsic defects KW - Partial density of states (pDOS) KW - Exciton KW - Polaron KW - Ligand-to-metal charge transfer KW - Aluminium oxide (Al₂O₃) KW - Hafnium oxide (HfO₂) KW - Titanium Oxide (TiO₂) Y1 - 2018 SN - 978-0-12-809739-7 SN - 978-0-12-814984-3 U6 - https://doi.org/10.1016/B978-0-12-409547-2.14119-8 SP - 162 EP - 171 PB - Elsevier CY - Oxford ER - TY - GEN A1 - Kot, Małgorzata A1 - Kegelmann, Lukas A1 - Das, Chittaranjan A1 - Kus, Peter A1 - Tsud, Nataliya A1 - Matolínová, Iva A1 - Albrecht, Steve A1 - Matolin, Vladimir A1 - Schmeißer, Dieter T1 - Room temperature atomic layer deposited Al₂O₃ improves perovskite solar cells efficiency over time T2 - ChemSusChem N2 - Electrical characterisation of perovskite solar cells consisting of room-temperature atomic-layer-deposited aluminium oxide (RT-ALD-Al₂O₃) film on top of a methyl ammonium lead triiodide (CH₃NH₃PbI₃) absorber showed excellent stability of the power conversion efficiency (PCE) over along time. Under the same environmental conditions (for 355 d), the average PCE of solar cells without the ALD layer decreased from 13.6 to 9.6 %, whereas that of solar cells containing 9 ALD cycles of depositing RT-ALD-Al₂O₃on top of CH₃NH₃PbI₃ increased from 9.4 to 10.8 %. Spectromicroscopic investigations of the ALD/perovskite interface revealed that the maximum PCE with the ALD layer is obtained when the so-called perovskite cleaning process induced by ALD precursors is complete. The PCE enhancement over time is probably related to a self-healing process induced by the RT-ALD-Al₂O₃ film. This work may provide a new direction for further improving the long-term stability and performance of perovskite solar cells. KW - Perovskite Solar Cells (PSCs) KW - Atomic layer deposition (ALD) KW - long time stabilty KW - X-Ray photoelectron spectroscopy (XPS) KW - Field-emission scanning electron microscopy (FESEM) Y1 - 2018 U6 - https://doi.org/10.1002/cssc.201801434 SN - 1864-5631 SN - 1864-564X VL - 11 IS - 20 SP - 3640 EP - 3648 ER - TY - GEN A1 - Kot, Małgorzata A1 - Gawlińska‐Nęcek, Katarzyna A1 - Henkel, Karsten A1 - Flege, Jan Ingo T1 - Prospects of improving efficiency and stability of hybrid perovskite solar cells by alumina ultrathin films T2 - Small N2 - Over the last few years, the influence of low temperature (≤80 °C) and, in particular, of room temperature, atomic layer deposited alumina (ALD‐Al2O3) on the properties of the underlying hybrid perovskites of different compositions and on the efficiency and stability of the corresponding perovskite solar cells (PSCs) is extensively investigated. The main conclusion is that most probably thanks to the presence of intrinsic defect states in the ALD‐Al2O3 and in the perovskite layers, charge transfer and neutralization are possible and the entire lifetime of the PSCs is thus improved. Moreover, the migration of mobile ions between the layers is blocked by the ALD‐Al2O3 layer and thus the occurrence of hysteresis in the current density–voltage characteristics of the PSCs is suppressed. Considering the uniform and nondestructive surface coverage, low thermal budget, small amount of material required, and short duration of the established ALD‐Al2O3 deposition on top of hybrid perovskites, this additional, but fully solar cell technology‐compatible, process step is most likely the most effective, cheapest, and fastest way to improve the efficiency and long‐term stability of PSCs and thus increase their marketability. KW - Perovskite solar cells (PSC) KW - Atomic layer deposition (ALD) KW - Photoelecton spectroscopy (PES) KW - Aluminum oxide Y1 - 2025 U6 - https://doi.org/10.1002/smll.202408435 SN - 1613-6810 VL - 21 IS - 12 PB - Wiley ER -