TY - GEN A1 - Mahmoodinezhad, Ali A1 - Pożarowska, Emilia A1 - Henkel, Karsten A1 - Schmeißer, Dieter A1 - Flege, Jan Ingo T1 - Depth profiling of PEALD-AlN films based on Al2p XPS peak decomposition T2 - Verhandlungen der DPG N2 - AlN has remarkable properties (wide band gap, low electrical and thermal conductivity, high dielectric constant, piezoelectricity) and is attractive for (opto)electronic and sensor applications. However, high oxygen content within nitride films is always a critical issue due to the thermodynamically favorable oxidation against nitridation resulting in deteriorated materials properties. In order to clarify whether the oxidation is a surface-limited or a bulk process elemental depth profiling is essential. In this work XPS in combination with Ar+ sputtering is applied to carry out depth profiling of AlN films prepared by plasma-enhanced atomic layer deposition using different parameters (plasma source, power and pulse duration). Particularly, the Al2p core levels are analyzed where the signals are decomposed into four components, representing weaker contributions of pure AlN and aluminum oxide phases as well as stronger signals of mixed oxygen-rich and nitrogen-rich phases. After sputtering (providing access to the deeper part of the film) the pure AlN phase content increases while the pure aluminum oxide content stays relatively constant. These issues are discussed with regard to the preparation parameters employed and accompanying XRD and electrical measurements. KW - X-Ray photoelectron spectroscopy (XPS) KW - peak decomposition KW - plasma enhanced atomic layer deposition (PEALD) KW - aluminium nitride (AlN) Y1 - 2019 UR - https://www.dpg-verhandlungen.de/year/2019/conference/regensburg/part/ds/session/14/contribution/25 SN - 0420-0195 SP - 157 EP - 157 PB - Deutsche Physikalische Gesellschaft CY - Bad Honnef ER - TY - GEN A1 - Nitsch, Paul-G. A1 - Ratzke, Markus A1 - Pozarowska, Emilia A1 - Flege, Jan Ingo A1 - Alvarado Chavarin, Carlos A1 - Wenger, Christian A1 - Fischer, Inga Anita T1 - Deposition of reduced ceria thin films by reactive magnetron sputtering for the development of a resistive gas sensor T2 - Verhandlungen der DPG, Berlin 2024 N2 - The use of cerium oxide for hydrogen sensing is limited by the low electrical conductivity of layers deposited from a ceria target. To increase the electrical conductivity, partially reduced cerium oxide layers were obtained from a metallic cerium target by reactive magnetron sputtering. The proportions of the oxidation states Ce3+, present in reduced species, and Ce4+, present in fully oxidized species, were determined by ex-situ XPS. For electrical characterization, films were deposited on planarized tungsten finger electrodes. IV curves were measured over several days to investigate possible influences of oxygen and humidity on electrical conductivity. The morphological stability of the layers under ambient conditions was investigated by microscopical methods. The XPS results show a significant amount of Ce3+ in the layers. The electrical conductivity of as-grown samples is several orders of magnitude higher than that of samples grown from a ceria target. However, the conductivity decreases over time, indicating an oxidation of the layers. The surface morphology of the samples was found to be changing drastically within days, leading to partial delamination. KW - ceria KW - metalic cerium target KW - electrical conductivity KW - X-ray photoelectron spectroscopy (XPS) KW - oxidation states KW - morphology Y1 - 2024 UR - https://www.dpg-verhandlungen.de/year/2024/conference/berlin/part/ds/session/11/contribution/18 SN - 0420-0195 PB - Deutsche Physikalische Gesellschaft CY - Bad Honnef ER -