TY - CHAP A1 - Sowinska, Małgorzata A1 - Das, Chittaranjan A1 - Wojciechowski, Konrad A1 - Snaith, Henry J. A1 - Schmeißer, Dieter T1 - XPS study of the ALD growth of Al₂O₃ on the CH₃NH₃PbI₃ T2 - Verhandlungen der Deutschen Physikalischen Gesellschaft N2 - Organic-inorganic lead halide perovskites have emerged as very attractive absorber materials for the fabrication of low cost and high efficiency solar cells, but a delicate nature of these films is one of the main challenges for a successful commercialization. Typically, when exposed to air or moisture, perovskite films degrade within a couple of hours or days. Moreover, the methylammonium lead triiodide (CH₃NH₃PbI₃) perovskite cannot sustain a prolonged annealing at temperatures around 85∘C. In this work, we are investigating stability (upon air and thermal exposure) of a CH₃NH₃PbI₃ perovskite film coated with a thin layer of Al₂O₃ deposited by atomic layer deposition (ALD). In particular, the chemical and electronic changes occurred at the Al₂O₃/CH₃NH₃PbI₃ interface during the first 50 ALD cycles were monitored ex-situ by high-resolution and surface-sensitive synchrotron-based X-ray photoelectron spectroscopy (SR-XPS). The advantage of the ALD as a deposition method is that it can produce extremely dense layers with a very precise thickness control at room temperature. Detailed SR-XPS data analysis and a stability test of the perovskite film with alumina will be presented. KW - atomic layer deposition KW - perovskite solar cells KW - Al₂O₃ KW - X-Ray photoelectron spectroscopy KW - synchrotron Y1 - 2016 UR - http://www.dpg-verhandlungen.de/year/2016/conference/regensburg/part/cpp/session/31/contribution/6?lang=en SP - S. 206 PB - Deutsche Physikalische Gesellschaft CY - Bad Honnef ER - TY - GEN A1 - Kot, Małgorzata A1 - Das, Chittaranjan A1 - Wang, Zhiping A1 - Henkel, Karsten A1 - Rouissi, Zied A1 - Wojciechowski, Konrad A1 - Snaith, Henry J. A1 - Schmeißer, Dieter T1 - Room-Temperature Atomic Layer Deposition of Al₂O₃: Impact on Efficiency, Stability and Surface Properties in Perovskite Solar Cells T2 - ChemSusChem N2 - In this work, solar cells with a freshly made CH₃NH₃PbI₃ perovskite film showed a power conversion efficiency (PCE) of 15.4 % whereas the one with 50 days aged perovskite film only 6.1 %. However, when the aged perovskite was covered with a layer of Al₂O₃ deposited by atomic layer deposition (ALD) at room temperature (RT), the PCE value was clearly enhanced. X-ray photoelectron spectroscopy study showed that the ALD precursors are chemically active only at the perovskite surface and passivate it. Moreover, the RT-ALD-Al2O3-covered perovskite films showed enhanced ambient air stability. KW - Al₂O₃ KW - atomic layer deposition (ALD) KW - perovskite KW - solar cells KW - X-ray photoelectron spectroscopy (XPS) Y1 - 2016 U6 - https://doi.org/10.1002/cssc.201601186 SN - 1864-5631 SN - 1864-564X VL - 9 IS - 24 SP - 3401 EP - 3406 ER - TY - GEN A1 - Kot, Małgorzata A1 - Das, Chittaranjan A1 - Henkel, Karsten A1 - Wojciechowski, Konrad A1 - Snaith, Henry J. A1 - Schmeißer, Dieter T1 - Room temperature atomic layer deposited Al₂O₃ on CH₃NH₃PbI₃ characterized by synchrotron-based X-ray photoelectron spectroscopy T2 - Nuclear Instruments and Methods in Physics Research B N2 - An ultrathin Al₂O₃ film deposited on methylammonium lead triiodide (CH₃NH₃PbI₃) perovskite has the capability to suppress the carrier recombination process and improve the perovskite solar cells efficiency and stability. However, annealing at temperatures higher than 85°C degrades the CH₃NH₃PbI₃ perovskite film. The X-ray photoelectron spectroscopy study performed in this work indicates that it is possible to grow Al₂O₃ by atomic layer deposition on the perovskite at room temperature, however, besides pure Al₂O₃ some OH groups are found and the creation of lead and iodine oxides at the Al₂O₃/CH₃NH₃PbI₃ interface takes place. KW - Synchrotron-based X-ray photoelectron spectroscopy KW - Perovskite solar cells KW - Atomic layer deposition KW - Al₂O₃ Y1 - 2017 U6 - https://doi.org/10.1016/j.nimb.2017.01.082 SN - 0168-583X SN - 1872-9584 VL - 411 SP - 49 EP - 52 ER -