TY - GEN A1 - Gomez-Alvarez, Miguel Angel A1 - Morales, Carlos A1 - Méndez, Javier A1 - Campo, Adolfo del A1 - Urbanos, Fernando J. A1 - Díaz, Aarón A1 - Reséndiz, Luis A1 - Flege, Jan Ingo A1 - Granados, Daniel A1 - Soriano, Leonardo T1 - A Comparative Study of the ZnO Growth on Graphene and Graphene Oxide: The Role of the Initial Oxidation State of Carbon T2 - C - Journal of Carbon Research N2 - The role of the oxidation state of carbon on the early stages of growth of metal oxides was studied for the particular case of ZnO deposition on graphene and graphene oxide on SiO2 (G/SiO2 and GO/SiO2, respectively) substrates. The growth was carried out by thermal evaporation of metallic Zn under an oxygen atmosphere at room temperature. This technique permits quasi-equilibrium conditions during the oxide growth, allowing the characterization of the fundamental interaction between ZnO and the graphene-based substrates. Although in both cases ZnO follows a Volmer–Weber growth mode controlled by nucleation at defects, the details are different. In the case of the GO/SiO2 substrate, the nucleation process acts as a bottleneck, limiting the coverage of the complete surface and allowing the growth of very large ZnO structures in comparison to G/SiO2. Moreover, by studying the Zn-LMM Auger spectra, it is shown how the initial nature of the substrate influences the composition of the ZnO deposit during the very early stages of growth in terms of Zn/O atomic ratio. These results are compared to those previously reported regarding ZnO growth on graphite and graphene on Cu (G/Cu). This comparison allows us to understand the role of different characteristics of graphene-based substrates in terms of number of defects, oxidation state, graphene support substrate and number of graphene layers. KW - graphene KW - graphene oxide KW - zinc oxide KW - intrefaces KW - mode of growth KW - x-Ray photoelectron spectroscopy (XPS) KW - atomic force microscopy (AFM) KW - factor analyis Y1 - 2020 U6 - https://doi.org/10.3390/c6020041 SN - 2311-5629 VL - 6 IS - 2 ER - TY - GEN A1 - Morales, Carlos A1 - Leinen, Dietmar A1 - Campo, Adolfo del A1 - Ares, José Ramón A1 - Sánchez, Carlos A1 - Flege, Jan Ingo A1 - Gutiérrez, Alejandro A1 - Prieto, Pilar A1 - Soriano, Leonardo T1 - Growth and characterization of ZnO thin films at low temperatures: from room temperature to -120 °C T2 - Journal of Alloys and Compounds N2 - ZnO thin films have been grown by e-beam evaporation in the range from room temperature to − 120 °C on two types of substrates, Al2O3 (0001) and Si (100). Although the ZnO/Al2O3 system has been thoroughly characterized, including optical and electrical techniques, the morphological, structural and chemical properties show no significant differences between both substrates. Thus, the general features of the ZnO growth mode at low temperature can be generalized. The relatively low growth temperatures reduce the diffusion of atoms at the surface, which leads to morphological and chemical changes. As the temperature decreases, the growth mode changes from a van der Drift model to a gradual bilayer system composed of an interfacial layer in contact with the substrate and a second columnar-based layer. This second well-ordered film disappears for the lowest temperatures while a Zn-rich interface in contact with the substrate emerges. Precisely from this interface, Zn-rich whiskers develop under the ZnO film and cause the loss of adhesion at temperatures below − 100 °C. These extreme temperatures also affect the crystal size, lattice strain, and total amount of oxygen vacancies. The behavior of the optical and electrical properties in terms of band gap, transparency, electrical resistivity, and Seebeck coefficient is discussed in the light of structural and chemical characterization. Samples grown at 0 °C exhibit an enhanced transmittance compared to those grown at room temperature while preserving similar electrical resistivity values and natural n-type doping. These results open a promising route to enhance ZnO films properties below the typical high temperature window. KW - zinc oxide (ZnO) KW - thin films KW - morphology KW - scanning electron microscopy (SEM) KW - DRX KW - optical properties KW - electrical properties Y1 - 2021 U6 - https://doi.org/10.1016/j.jallcom.2021.161056 SN - 0925-8388 SN - 1873-4669 VL - 884 ER -