TY - CHAP A1 - Cuypers, Daniel A1 - Dorp, Dennis H. von A1 - Tallarida, Massimo A1 - Brizzi, Simone A1 - Rodriguez, Leonard A1 - Conard, Thierry A1 - Arnauts, Sophia A1 - Schmeißer, Dieter A1 - Adelmann, Christoph A1 - De Gendt, Stefan T1 - Study of InP Surfaces After Wet Chemical Treatments T2 - Meeting Abstracts-Electrochemical Society, San Francisco, 2013 KW - Synchrotron Radiation Photoelectron Spectroscopy KW - InP KW - Wet chemical treatment Y1 - 2013 UR - http://ma.ecsdl.org/content/MA2013-02/30/2132.full.pdf+html N1 - MA2013-02(30) SP - S. 2132 PB - The Electrochemical Society ER - TY - GEN A1 - Cuypers, Daniel A1 - Dorp, Dennis H. von A1 - Tallarida, Massimo A1 - Brizzi, Simone A1 - Rodriguez, Leonard A1 - Conard, Thierry A1 - Arnauts, Sophia A1 - Schmeißer, Dieter A1 - Adelmann, Christoph A1 - De Gendt, Stefan T1 - Study of InP Surfaces after Wet Chemical Treatments T2 - ECS Transactions N2 - In this work synchrotron radiation photoemission spectroscopy (SRPES) is used to study InP surfaces after different wet chemical treatments. All results are compared to a typical fingerprint of surface components present on an as received InP sample. It is shown that acidified (HCl and H₂SO₄) treatments efficiently remove the native phosphate, although components like Pᴼ, Inᴼ and P(2±∆)+ remain present. In alkaline solution (NH₄OH) oxide remains present at the surface. As an alternative treatment, the immersion into (NH₄)₂S was studied. This passivation treatment results in fewer surface components which suggests that a higher quality surface is obtained. KW - Synchrotron Radiation Photoelectron Spectroscopy KW - InP KW - Wet chemical treatment Y1 - 2013 U6 - https://doi.org/10.1149/05806.0297ecst SN - 1938-6737 SN - 1938-5862 VL - 58 IS - 6 SP - 297 EP - 303 ER - TY - GEN A1 - Cuypers, Daniel A1 - Dorp, Dennis H. von A1 - Tallarida, Massimo A1 - Brizzi, Simone A1 - Conard, Thierry A1 - Rodriguez, Leonard A1 - Mees, M. A1 - Arnauts, Sophia A1 - Schmeißer, Dieter A1 - Adelmann, Christoph A1 - De Gendt, Stefan T1 - Study of InP Surfaces after Wet Chemical Treatments T2 - ECS Journal of Solid State Science and Technology N2 - The influence of different wet chemical treatments (HCl, H₂SO₄, NH₄OH) on the composition of InP surfaces is studied by using synchrotron radiation photoemission spectroscopy (SRPES). It is shown that a significant amount of oxide remains present after immersion in a NH₄OH solution which is ascribed to the insolubility of In³⁺ at higher pH values. Acidic treatments efficiently remove the native oxide, although components like Pᴼ, Inᴼ and P(2±Δ)+ suboxides are observed. Alternatively, the influence of a passivation step in (NH₄)₂S solution on the surface composition was investigated. The InP surface after immersion into (NH₄)₂S results in fewer surface components, without detection of Pᴼ and P(2±Δ)+ suboxides. Finally, slight etching of InP surfaces in HCl/H₂O₂ solution followed by a native oxide removal step, showed no significant effect on the surface composition. KW - Synchrotron Radiation Photoelectron Spectroscopy KW - Scanning Tunneling Microscopy KW - InP KW - Wet chemical treatment Y1 - 2014 U6 - https://doi.org/10.1149/2.005401jss SN - 2162-8777 SN - 2162-8769 VL - 3 IS - 1 SP - N3016 EP - N3022 ER - TY - GEN A1 - Dorp, Dennis H. von A1 - Nyns, Laura A1 - Cuypers, Daniel A1 - Ivanov, Tsvetan A1 - Brizzi, Simone A1 - Tallarida, Massimo A1 - Fleischmann, Claudia A1 - Hönicke, Philipp A1 - Müller, Matthias A1 - Richard, Olivier A1 - Schmeißer, Dieter A1 - De Gendt, Stefan A1 - Lin, Dennis H. C. A1 - Adelmann, Christoph T1 - Amorphous Gadolinium Aluminate as a Dielectric and Sulfur for Indium Phosphide Passivation T2 - ACS Applied Electronic Materials N2 - The passivation of n-type InP (100) using sulfur in combination with a gadolinium aluminate (GAO) dielectric layer has been studied. Photoluminescence, minority-carrier lifetime, and capacitance−voltage measurements indicate that a (NH4)2S vapor passivation step prior to atomic layer deposition of the oxide effectively lowers the interface state density. Surface and interface chemistry were studied by synchrotron radiation photoemission spectroscopy (SRPES). The effect of ex situ surface passivation after native oxide removal in HCl solution was examined. It was observed that surface reoxidation occurred during (NH4)2S vapor exposure, leading to the formation of Inx(HPO4)y. S was present on the surface as a sulfide in both surface and subsurface sites. After atomic layer deposition of GAO, sulfates were detected in addition to Inx(HPO4)y, which was confirmed by near-edge X-ray absorptionfine structure analysis. The S in the stack was quantified using reference-free grazing incidence X-rayfluorescence analysis. X-ray absorption spectroscopy showed that Gd was oxidized and present in the 3+ oxidation state, most likely as a phosphate close to the InP interface and possibly mixed with sulfates. Energy-dependent SRPES measurements of Al 2p and Gd 4d core levels, complemented by transmission electron microscopy, further suggest that the dielectric layer was segregated. Valence band measurements confirm the effective passivation of InP, indicating unpinning of the surface Fermi level. KW - III−V KW - InP KW - sulfur passivation KW - atomic layer deposition KW - gadolinium aluminate KW - rare earth oxide KW - dielectric Y1 - 2019 U6 - https://doi.org/10.1021/acsaelm.9b00388 SN - 2637-6113 VL - 1 IS - 11 SP - 2190 EP - 2201 ER -