TY - CHAP A1 - Cuypers, Daniel A1 - Dorp, Dennis H. von A1 - Tallarida, Massimo A1 - Brizzi, Simone A1 - Rodriguez, Leonard A1 - Conard, Thierry A1 - Arnauts, Sophia A1 - Schmeißer, Dieter A1 - Adelmann, Christoph A1 - De Gendt, Stefan T1 - Study of InP Surfaces After Wet Chemical Treatments T2 - Meeting Abstracts-Electrochemical Society, San Francisco, 2013 KW - Synchrotron Radiation Photoelectron Spectroscopy KW - InP KW - Wet chemical treatment Y1 - 2013 UR - http://ma.ecsdl.org/content/MA2013-02/30/2132.full.pdf+html N1 - MA2013-02(30) SP - S. 2132 PB - The Electrochemical Society ER - TY - GEN A1 - Cuypers, Daniel A1 - Dorp, Dennis H. von A1 - Tallarida, Massimo A1 - Brizzi, Simone A1 - Rodriguez, Leonard A1 - Conard, Thierry A1 - Arnauts, Sophia A1 - Schmeißer, Dieter A1 - Adelmann, Christoph A1 - De Gendt, Stefan T1 - Study of InP Surfaces after Wet Chemical Treatments T2 - ECS Transactions N2 - In this work synchrotron radiation photoemission spectroscopy (SRPES) is used to study InP surfaces after different wet chemical treatments. All results are compared to a typical fingerprint of surface components present on an as received InP sample. It is shown that acidified (HCl and H₂SO₄) treatments efficiently remove the native phosphate, although components like Pᴼ, Inᴼ and P(2±∆)+ remain present. In alkaline solution (NH₄OH) oxide remains present at the surface. As an alternative treatment, the immersion into (NH₄)₂S was studied. This passivation treatment results in fewer surface components which suggests that a higher quality surface is obtained. KW - Synchrotron Radiation Photoelectron Spectroscopy KW - InP KW - Wet chemical treatment Y1 - 2013 U6 - https://doi.org/10.1149/05806.0297ecst SN - 1938-6737 SN - 1938-5862 VL - 58 IS - 6 SP - 297 EP - 303 ER - TY - GEN A1 - Cuypers, Daniel A1 - Dorp, Dennis H. von A1 - Tallarida, Massimo A1 - Brizzi, Simone A1 - Conard, Thierry A1 - Rodriguez, Leonard A1 - Mees, M. A1 - Arnauts, Sophia A1 - Schmeißer, Dieter A1 - Adelmann, Christoph A1 - De Gendt, Stefan T1 - Study of InP Surfaces after Wet Chemical Treatments T2 - ECS Journal of Solid State Science and Technology N2 - The influence of different wet chemical treatments (HCl, H₂SO₄, NH₄OH) on the composition of InP surfaces is studied by using synchrotron radiation photoemission spectroscopy (SRPES). It is shown that a significant amount of oxide remains present after immersion in a NH₄OH solution which is ascribed to the insolubility of In³⁺ at higher pH values. Acidic treatments efficiently remove the native oxide, although components like Pᴼ, Inᴼ and P(2±Δ)+ suboxides are observed. Alternatively, the influence of a passivation step in (NH₄)₂S solution on the surface composition was investigated. The InP surface after immersion into (NH₄)₂S results in fewer surface components, without detection of Pᴼ and P(2±Δ)+ suboxides. Finally, slight etching of InP surfaces in HCl/H₂O₂ solution followed by a native oxide removal step, showed no significant effect on the surface composition. KW - Synchrotron Radiation Photoelectron Spectroscopy KW - Scanning Tunneling Microscopy KW - InP KW - Wet chemical treatment Y1 - 2014 U6 - https://doi.org/10.1149/2.005401jss SN - 2162-8777 SN - 2162-8769 VL - 3 IS - 1 SP - N3016 EP - N3022 ER - TY - GEN A1 - Adelmann, Christoph A1 - Schram, Tom A1 - Chew, Soon Aik A1 - Woicik, J. C. A1 - Brizzi, Simone A1 - Tallarida, Massimo A1 - Schmeißer, Dieter A1 - Horiguchi, Naoto A1 - Elshocht, Sven van A1 - Ragnarsson, Lars-Åke T1 - On the scalability of doped hafnia thin films T2 - Applied Physics Letters N2 - The scaling behavior of Gd- and Al-doped HfO2 films as gate dielectrics in metal-oxide-semiconductor (MOS) capacitors was studied. For equivalent oxide thicknesses (EOTs) in the range of 10 Å, crystallized Gd:HfO2 showed higher leakage current densities than crystallized Al:HfO2, with undoped HfO2 in between. Ultimately, the scalability of Al:HfO2 was limited by the ability to crystallize the films at a given thermal budget. As a result, for post-deposition annealing at 800 °C, the EOT of Al:HfO2 based MOS capacitors was limited to ∼8 Å. However, for such an EOT, leakage current densities were reduced by about 100× with respect to HfO2. This demonstrates the high potential of Al:HfO2 for low-standby-power MOS devices. KW - scalability KW - hafnia thin films KW - Al:HfO2 KW - Gd:HfO2 KW - EXAFS KW - equivalent oxide thickness (EOT) KW - leakage current KW - X-ray absorption spectroscopy (XAS) Y1 - 2014 U6 - https://doi.org/10.1063/1.4870075 SN - 0003-6951 SN - 1077-3118 IS - 104 SP - 122906-1 EP - 122906-4 ER - TY - GEN A1 - Nourbakhsh, Amirhasan A1 - Adelmann, Christoph A1 - Song, Yi A1 - Lee, Chang Seung A1 - Asselberghs, Inge A1 - Huyghebaert, Cedric A1 - Brizzi, Simone A1 - Tallarida, Massimo A1 - Schmeißer, Dieter A1 - Elshocht, Sven van A1 - Heyns, Marc A1 - Kong, Jing A1 - Palacios, Tomás A1 - De Gendt, Stefan T1 - Graphene oxide monolayers as atomically thin seeding layers for atomic layer deposition of metal oxides T2 - Nanoscale N2 - Graphene oxide (GO) was explored as an atomically-thin transferable seed layer for the atomic layer deposition (ALD) of dielectric materials on any substrate of choice. This approach does not require specific chemical groups on the target surface to initiate ALD. This establishes GO as a unique interface which enables the growth of dielectric materials on a wide range of substrate materials and opens up numerous prospects for applications. In this work, a mild oxygen plasma treatment was used to oxidize graphene monolayers with well-controlled and tunable density of epoxide functional groups. This was confirmed by synchrotron-radiation photoelectron spectroscopy. In addition, density functional theory calculations were carried out on representative epoxidized graphene monolayer models to correlate the capacitive properties of GO with its electronic structure. Capacitance–voltage measurements showed that the capacitive behavior of Al2O3/GO depends on the oxidation level of GO. Finally, GO was successfully used as an ALD seed layer for the deposition of Al2O3 on chemically inert single layer graphene, resulting in high performance top-gated field-effect transistors. KW - Graphene Oxide KW - seed layer KW - atomic layer deposition KW - oxygen plasma treatment KW - photoelectron spectroscopy KW - density functional theory KW - capacitance-voltage Y1 - 2015 U6 - https://doi.org/10.1039/C5NR01128K SN - 2040-3364 SN - 2040-3372 VL - 2015 IS - 7 SP - 10781 EP - 10789 ER - TY - GEN A1 - Alberton Corrêa, Silma A1 - Brizzi, Simone A1 - Schmeißer, Dieter T1 - Spectroscopic investigation of the electronic structure of thin atomic layer deposition HfO2 films T2 - Journal of Vacuum Science & Technology A N2 - The electronic structure of HfO2 thin films is investigated employing resonant photoelectron spectroscopy (resPES). The detailed analysis of the O1s resonance profile enables the determination of the partial density of states for the valence and the conduction bands as well as the electronic band gap to be 6.2 eV. The position of the charge neutrality level is evaluated. Thereby, it is demonstrated that the resPES data are able to combine information both for the valence as well as for the conduction band states. In addition, evidences for intrinsic in-gap states attributed to polaronic and charge transfer states are given. Electronic charges within the atomic layer deposition-HfO2films are identified, pointing out that the amount of charges is essential to determine the accurate position of the surface potentials. KW - resonant photoelectron spectroscopy KW - hafnium oxide KW - atomic layer deposition KW - partial density of states KW - electronic band gap Y1 - 2016 U6 - https://doi.org/10.1116/1.4935338 SN - 0734-2101 SN - 1520-8559 VL - 34 IS - 1 SP - 01A117-1 EP - 01A117-8 ER - TY - CHAP A1 - Alberton Corrêa, Silma A1 - Brizzi, Simone A1 - Tallarida, Massimo A1 - Schmeißer, Dieter T1 - Charging effect in HfO2 films deposited on SiO2/Si by atomic layer deposition T2 - Verhandlungen der Deutschen Physikalischen Gesellschaft N2 - Thin films of hafnium oxide (HfO2) deposited by atomic layer deposition (ALD) have been studied extensively as a high-k replacement for the SiO2 gate in field effect transistors. The use of ALD process allows one to grow homogeneous thin films at low temperatures with a precise control of thickness [1]. Some important electrical considerations for the application of a high-k dielectric include the presence of fixed charge (Qf) and charge trapping in the dielectric. For instance, in the case of Al2O3 thin films deposited on Si, the thickness of the interfacial SiO2 layer was identified as a key fundamental parameter determining Qf [2]. A similar trend can be also expected in HfO2/Si structures. Therefore, in this work, we proposed an in situ evaluation of photon induced charge trapping in HfO2 films deposited on SiO2/Si structures. For that, tetrakis-di-methyl-amino-hafnium (TDMAHf) and H2O were employed as precursors to deposit HfO2 films on SiO2/Si samples with variable thickness of the SiO2 interlayer. Measurements were performed by Synchrotron Radiation Photoemission Spectroscopy (SR-PES). Results indicated that the charging process is dependent on the thickness of the SiO2 interlayer and on the quality of the HfO2 film. [1] M. Leskelä and M. Ritala, Thin Solid Films 409, 138 (2002). [2] G. Dingemans et al., J. Appl. Phys. 110, 093715 (2011). KW - Charging KW - HfO2 KW - atomic layer deposition (ALD) Y1 - 2014 UR - http://www.dpg-verhandlungen.de/year/2014/conference/dresden/part/ds/session/49/contribution/10?lang=en SN - 0420-0195 PB - Deutsche Physikalische Gesellschaft CY - Bad Honnef ER - TY - CHAP A1 - Brizzi, Simone A1 - Tallarida, Massimo A1 - Adelmann, Christoph A1 - Ragnarsson, Lars-Åke A1 - Elshocht, Sven van A1 - Schmeißer, Dieter T1 - Structural changes in HfO2 thin films: thickness and doping dependence T2 - Verhandlungen der Deutschen Physikalischen Gesellschaft N2 - In this work we show results regarding MOCVD and ALD HfO2 as well as Al-doped HfO2. We use Synchrotron Radiation Photoemission Spectroscopy (SRPES) to determine Hf/O atomic ratios and X-ray Absorption Spectroscopy (XAS) to investigate the electronic properties related to their crystallization. MOCVD films are synthesized at temperatures ranging from ambient to 400∘C and show structures from completely amorphous to monoclinic. ALD films are amorphous as deposited, and can crystallize after post-deposition anneal depending on the percentage of Al-doping. We discuss PES results in order to determine how close to stoichiometry the Hf/O atomic ratios of the films are, as well as the doping level. From XAS data, instead, we can point out how orbital hybridizations are related to structural and physical properties. KW - Structure KW - HfO2 thin films KW - thickness dependence KW - doping dependence KW - atomic layer deposition (ALD) Y1 - 2014 UR - http://www.dpg-verhandlungen.de/year/2014/conference/dresden/part/ds/session/49/contribution/9?lang=en SN - 0420-0195 PB - Deutsche Physikalische Gesellschaft CY - Bad Honnef ER - TY - CHAP A1 - Alberton Corrêa, Silma A1 - Brizzi, Simone A1 - Tallarida, Massimo A1 - Schmeißer, Dieter T1 - Spectroscopic investigation of the electronic structure of HfO2 thin films T2 - Verhandlungen der Deutschen Physikalischen Gesellschaft N2 - HfO2 is of current interest as a material for memristive and ferroelectric devices. In this work, we used spectroscopic techniques to evaluate the electronic structure and defects mechanisms in thin HfO2 films deposited by atomic layer deposition and by metal-organic chemical vapour deposition. The partial density of states for the valence and the conduction bands was determined by the detailed analysis of the O1s resonance profile by resonant photoelectron spectroscopy. From the relative contributions we find a CNL 6.5 eV referred to Evac. We also find that the positions of valence band maximum and conduction band minimum, the excitation range for the polaronic states and the range of charge transfer band were not influenced by the preparation conditions. All films exhibit a band gap of 6.2 eV. However, the Fermi level position was found to vary within about 1.2 eV depending on the preparation conditions, which we argue that is due to the presence of charges within the films. This explains why the position of the Fermi level depends on the individual preparation parameters. KW - electronic structure KW - HfO2 Y1 - 2015 UR - http://www.dpg-verhandlungen.de/year/2015/conference/berlin/part/ds/session/36/contribution/106?lang=en SN - 0420-0195 SP - S. 211 PB - Deutsche Physikalische Gesellschaft CY - Bad Honnef ER - TY - CHAP A1 - Rouissi, Zied A1 - Brizzi, Simone A1 - Alberton Corrêa, Silma A1 - Tallarida, Massimo A1 - Schmeißer, Dieter T1 - Comparison of charge neutrality level of Cu/CuO/HfO2 and Si/SiO2/HfO2 T2 - Verhandlungen der Deutschen Physikalischen Gesellschaft N2 - Copper Oxide (CuO) is a promising metal oxide semiconductor, which can be used in different applications, such as catalysis, solar energy conversion, and water splitting. In this work, we use resonance photoemission spectroscopy (ResPES) to analyse the electronics properties of HfO2 films deposited on Cu/CuO and Si/SiO2. For that, we deposited 10 cycles of HfO2 by atomic layer deposition (ALD) on Cu/CuO and Si/SiO2 samples and investigated the density states for the valence and conduction bands which were determined by the detailed analysis of the O1s resonance profile obtained by ResPES. We compared the positions of valence band maximum and conduction band minimum, the excitation range for the polaronic states and the range of charge transfer band in Cu/CuO/HfO2 and Si/SiO2/HfO2. Also, we determined the band gap and the charge neutrality level (CNL). KW - charge neutrality level (CNL) KW - resonant photoelectron spectroscopy KW - HfO2 Y1 - 2015 UR - http://www.dpg-verhandlungen.de/year/2015/conference/berlin/part/ds/session/36/contribution/47?lang=en SN - 0420-0195 SP - 208 PB - Deutsche Physikalische Gesellschaft CY - Bad Honnef ER - TY - GEN A1 - Sowinska, Małgorzata A1 - Brizzi, Simone A1 - Das, Chittaranjan A1 - Kärkkänen, Irina A1 - Schneidewind, Jessica A1 - Naumann, Franziska A1 - Gargouri, Hassan A1 - Henkel, Karsten A1 - Schmeißer, Dieter T1 - Analysis of nitrogen species in titanium oxynitride ALD films T2 - Applied Surface Science N2 - Titanium oxynitride films are prepared by plasma enhanced atomic layer deposition method using two different precursors and nitrogen sources. Synchrotron radiation-based X-ray photoelectron spectroscopy and X-ray absorption spectroscopy are used to characterize the nitrogen species incorporated within these films depending on the deposition parameters. It is found that nitrogen atoms in these films are differently bonded. In particular, it can be distinguished between Ti-ON and Ti-N bonding configurations and molecular nitrogen species caused by precursor fragments. KW - titanium oxynitride KW - X-ray photoelectron spectroscopy KW - X-ray absorption spectroscopy KW - ALD process parameters Y1 - 2016 U6 - https://doi.org/10.1016/j.apsusc.2016.02.096 SN - 0169-4332 SN - 1873-5584 VL - 381 SP - 42 EP - 47 ER - TY - CHAP A1 - Brizzi, Simone A1 - Tallarida, Massimo A1 - Schmeißer, Dieter T1 - CVD and ALD deposited hafnia: an XPS study T2 - Verhandlungen der Deutschen Physikalischen Gesellschaft N2 - In this work we report on Hafnium oxide deposited on silicon by means of chemical vapour deposition (CVD) and atomic layer deposition (ALD) using tetrakis-di-methyl-amino-Hf (TDMAHf) and water as precursors. We have studied the behavior of ALD and CVD at intermediate temperatures: ALD was performed outside the ALD window (T>300∘C), whereas CVD was performed at low temperatures, approaching the ALD window (T<400∘C). In this way we wanted to elucidate about the possibility of taking advantage of the conformality of ALD films and the high growth rate of CVD at the same time. Comparable sets of samples prepared with the two methods were measured by X-ray photoelectron spectroscopy and atomic force microscopy in order to determine differences between them: growth rate, Hf/O ratio, valence band positions and roughness are discussed and compared as a function of deposition temperature and process parameters. KW - HfO2 KW - chemical vapor deposition KW - atomic layer deposition (ALD) KW - X-Ray photoelectron spectroscopy Y1 - 2013 UR - http://www.dpg-verhandlungen.de/year/2013/conference/regensburg/part/ds/session/30/contribution/1?lang=de PB - Deutsche Physikalische Gesellschaft CY - Bad Honnef ER - TY - GEN A1 - Haeberle, Jörg A1 - Brizzi, Simone A1 - Gaspar, Diana A1 - Barquinha, Pedro A1 - Galazka, Zbigniew A1 - Schulz, Detlev A1 - Schmeißer, Dieter T1 - A spectroscopic comparison of IGZO thin film and the parent In2O3, Ga2O3, and ZnO single crystals T2 - Materials Research Express N2 - We use resonant photoelectron spectroscopy at the Zn 2p, Ga 2p, In 3d, and O 1s absorption edges to report on the electronic properties of indium–gallium–zinc-oxide thin films. We also compare the data with the respective data of the corresponding single crystals In2O3, Ga2O3, and ZnO. We focus on the elemental composition and, in particular, find no evidence for oxygen deficiency. The In, Ga, and Zn absorption data at resonance can be used to analyze the conduction band states in detail. We deduce that a configuration interaction between d10s0 and d9s1states is of importance. We provided a novel mechanism in which configuration interaction induced gap states create both, extended unoccupied states around E F as well as localized occupied states within the gap. KW - transparent conducting oxides (TCO) KW - resonant photoelectron spectroscopy KW - in-gapdefect states Y1 - 2016 U6 - https://doi.org/10.1088/2053-1591/3/10/106302 SN - 2053-1591 VL - 3 IS - 10 SP - 106302-1 EP - 106302-17 ER - TY - GEN A1 - Cuypers, Daniel A1 - Fleischmann, Claudia A1 - Dorp, Dennis H. von A1 - Brizzi, Simone A1 - Tallarida, Massimo A1 - Müller, Matthias A1 - Hönicke, Philipp A1 - Billen, Arne A1 - Chintala, Ravi A1 - Conard, Thierry A1 - Schmeißer, Dieter A1 - Vandervorst, Wilfried A1 - Elshocht, Sven van A1 - Armini, Silvia A1 - De Gendt, Stefan A1 - Adelmann, Christoph T1 - Sacrificial Self-Assembled Monolayers for the Passivation of GaAs(100) Surfaces and Interfaces T2 - Chemistry of Materials N2 - The use of sacrificial self-assembled monolayers (SAMs) to prepare clean n-type GaAs (100) surfaces without band bending in vacuo is demonstrated. GaAs surface passivation using octadecanethiol SAMs after HCl cleaning is shown to lead to an enhancement of the room-temperature photoluminescence intensity. Synchrotron-radiation photoelectron spectroscopy (SRPES) finds that the interfacial oxide between GaAs and the SAM remains below the detection limit. Evidence for both Ga–S and As–S bonds at the GaAs–thiolate interface is found. The limited thermal stability of the SAM allows the desorption of the alkyl chains by in situ thermal annealing at temperatures above 180 °C, leaving S bonded to Ga behind. The resulting surface contains only a very small amount of O (0.05 ML coverage) and C (about 3% of the SAM remaining) and shows no band bending with the surface Fermi level close to the conduction band. Atomic layer deposition of Al₂O₃ on this surface occurs via the formation of Al–S bonds without introducing any additional band bending. This indicates that the surface preparation of n-type GaAs (100) using sacrificial octadecanethiol SAMs followed by in situ thermal removal provides a route toward GaAs/oxide interfaces without interfacial oxides and without band bending. KW - GaAs KW - passivation KW - Al₂O₃ KW - atomic layer deposition (ALD) KW - Synchrotron-radiation photoelectron spectroscopy (SRPES) KW - self assembled monolayers (SAM) KW - interface engineering Y1 - 2016 U6 - https://doi.org/10.1021/acs.chemmater.6b01732 SN - 0897-4756 SN - 1520-5002 VL - 28 IS - 16 SP - 5689 EP - 5701 ER - TY - GEN A1 - Corrêa, Silma Alberton A1 - Brizzi, Simone A1 - Schmeißer, Dieter T1 - Depicting the Electronic Structure of HfO₂ Films by Spectroscopic Techniques T2 - ECS Transactions N2 - The electronic structure of HfO₂ films was investigated. The partial density of states for the valence and the conduction bands was determined by the detailed analysis of the O1s resonance profile by resonant photoelectron spectroscopy. The positions of valence band maximum and conduction band minimum, the excitation range for the polaronic states and the range of charge transfer band were found to be not influenced by the preparation conditions. The band gap was determined to be 6.2 eV and the energy of the charge neutrality level (referred to vacuum level) was determined as 4.7 eV. The Fermi level position was observed to vary about 1.2 eV depending on the preparation conditions, which indicates the presence of charges within the films. KW - HfO₂ KW - resonant photoelectron spectroscopy (resPES) KW - electronic structure KW - partial density of states KW - charge neutrality level Y1 - 2016 U6 - https://doi.org/10.1149/07506.0145ecst SN - 1938-6737 SN - 1938-5862 VL - 75 IS - 6 SP - 145 EP - 153 ER - TY - GEN A1 - Kot, Małgorzata A1 - Henkel, Karsten A1 - Das, Chittaranjan A1 - Brizzi, Simone A1 - Kärkkänen, Irina A1 - Schneidewind, Jessica A1 - Naumann, Franziska A1 - Gargouri, Hassan A1 - Schmeißer, Dieter T1 - Analysis of titanium species in titanium oxynitride films prepared by plasma enhanced atomic layer deposition T2 - Surface and Coatings Technology N2 - A comparative study of thin titanium oxynitride (TiOxNy) films prepared by plasma enhanced atomic layer deposition using tetrakis(dimethylamino)titanium (TDMAT) and N2 plasma as well as titanium(IV)isopropoxide and NH3 plasma is reported. The comparison is based on the combination of Ti2p core level and valence band spectroscopy and current-voltage measurements. The TDMAT/N2 process delivers generally higher fractions of TiN and TiON within the Ti2p spectra of the films and stronger photoemissions within the bandgap as resolved in detail by high energy resolution synchrotron-based spectroscopy. In particular, it is shown that higher TiN contributions and in-gap emission intensities correlate strongly with increased leakage currents within the films and might be modified by the process parameters and precursor selection. KW - Titanium oxynitride KW - Plasma enhanced atomic layer deposition (PEALD) KW - ALD process parameters KW - Ti-N contributions KW - In-gap defect states KW - Leakage current Y1 - 2017 U6 - https://doi.org/10.1016/j.surfcoat.2016.11.094 SN - 0257-8972 SN - 1879-3347 VL - 324 SP - 586 EP - 593 ER - TY - GEN A1 - Dorp, Dennis H. von A1 - Nyns, Laura A1 - Cuypers, Daniel A1 - Ivanov, Tsvetan A1 - Brizzi, Simone A1 - Tallarida, Massimo A1 - Fleischmann, Claudia A1 - Hönicke, Philipp A1 - Müller, Matthias A1 - Richard, Olivier A1 - Schmeißer, Dieter A1 - De Gendt, Stefan A1 - Lin, Dennis H. C. A1 - Adelmann, Christoph T1 - Amorphous Gadolinium Aluminate as a Dielectric and Sulfur for Indium Phosphide Passivation T2 - ACS Applied Electronic Materials N2 - The passivation of n-type InP (100) using sulfur in combination with a gadolinium aluminate (GAO) dielectric layer has been studied. Photoluminescence, minority-carrier lifetime, and capacitance−voltage measurements indicate that a (NH4)2S vapor passivation step prior to atomic layer deposition of the oxide effectively lowers the interface state density. Surface and interface chemistry were studied by synchrotron radiation photoemission spectroscopy (SRPES). The effect of ex situ surface passivation after native oxide removal in HCl solution was examined. It was observed that surface reoxidation occurred during (NH4)2S vapor exposure, leading to the formation of Inx(HPO4)y. S was present on the surface as a sulfide in both surface and subsurface sites. After atomic layer deposition of GAO, sulfates were detected in addition to Inx(HPO4)y, which was confirmed by near-edge X-ray absorptionfine structure analysis. The S in the stack was quantified using reference-free grazing incidence X-rayfluorescence analysis. X-ray absorption spectroscopy showed that Gd was oxidized and present in the 3+ oxidation state, most likely as a phosphate close to the InP interface and possibly mixed with sulfates. Energy-dependent SRPES measurements of Al 2p and Gd 4d core levels, complemented by transmission electron microscopy, further suggest that the dielectric layer was segregated. Valence band measurements confirm the effective passivation of InP, indicating unpinning of the surface Fermi level. KW - III−V KW - InP KW - sulfur passivation KW - atomic layer deposition KW - gadolinium aluminate KW - rare earth oxide KW - dielectric Y1 - 2019 U6 - https://doi.org/10.1021/acsaelm.9b00388 SN - 2637-6113 VL - 1 IS - 11 SP - 2190 EP - 2201 ER -