TY - GEN A1 - Fellah, Mamoun A1 - Hezil, Naouel A1 - Samad, Mohammed Abdul A1 - Touhami, Mohamed Zine A1 - Montagne, Alex A1 - Iost, Alain A1 - Obrosov, Aleksei A1 - Weiß, Sabine T1 - Preliminary investigation on the bio-tribocorrosion behavior of porous nanostructured β-type titanium based biomedical alloys T2 - Materials Letters N2 - The bio-tribocorrosion behavior of newly developed near β-types Ti-15Nb and Ti-15Mo alloys was investigated in Phosphate-Buffered Saline (PBS) under different loads. Open-Circuit Potential (OCP), friction coefficient, wear volume and wear rate were evaluated. The results revealed that Ti-15Nb alloy exhibited lower wear rate, lower friction coefficient and better corrosion resistance during tribocorrosion than the Ti-15Mo alloy. This can be attributed to the diffusion of Nb which increases the repassivation rate (formation of a protective layer) in the Ti-15Nb alloy. In contrast Ti-15Mo shows a significantly higher rate of chemical reaction. KW - Ti-15Mo KW - Ti-15Nb KW - Corrosion KW - Bio-tribocorrosion KW - Biomaterials Y1 - 2019 UR - https://www.sciencedirect.com/science/article/pii/S0167577X19313862 U6 - https://doi.org/10.1016/j.matlet.2019.126755 SN - 0167-577X VL - 257 ER - TY - GEN A1 - Fouzia, Hammadi A1 - Fellah, Mamoun A1 - Hezil, Naouel A1 - Aissani, Linda A1 - Mimanne, Goussem A1 - Mechachti, Said A1 - Samad, Mohammed Abdul A1 - Montagne, Alex A1 - Iost, Alain A1 - Weiß, Sabine A1 - Obrosov, Aleksei T1 - The effect of milling time on the microstructure and mechanical properties of Ti-6Al-4Fe alloys T2 - Materials Today Communications N2 - Replacement of toxic and expensive vanadium (V) in medical grade titanium alloys with cheaper and non-toxic elements such as iron (Fe) or niobium (Nb), is an important step forward in developing safer and less expensive biomaterials. Evaluating the effect of different process parameters such as the milling time on the properties of these newly developed alloys helps in understanding and controlling their behavior. Hence, in this study, the influence of ball-milling duration (2, 6, 8, 12 and 18 h) on crystalline structure, phase evolution, densification, and mechanical characteristics of biomedical nanocrystalline Ti-6Al-4Fe (wt. %) alloys is investigated. X-ray diffraction (XRD) confirmed that after 6 h of milling, aluminum (Al) and Fe completely dissolved into Ti matrix to form a solid solution of Ti (Al, Fe). XRD further revealed that the crystallite size decreased from 56 to 30 nm and the micro-strain increased with an increase in milling time. A decrease in porosity along with an increase in density is also observed for the alloys with increasing milling time. Moreover, the values of porosity obtained for the developed Ti-6Al-4Fe alloys ranged from 1 to 12 %, which is comparable to the porosity of one of the cortical bones making it a potential candidate for bone replacements. Microhardness measurements showed that the hardness of the Ti-6Al-4Fe alloys was greater than the hardness of the conventional Ti-6Al-4V alloys. It was observed that the Ti-6Al-4Fe alloy fabricated with the powders milled for 2 h showed the lowest value of Young’s Modulus. Milling time also had a significant effect on the surface roughness of the alloy samples, which showed a decreasing trend with increasing milling times. KW - Ti-based alloys KW - Microstructure KW - Mechanical properties KW - Ball-milling KW - Biomaterials KW - Milling time Y1 - 2021 UR - https://www.sciencedirect.com/science/article/abs/pii/S2352492821004207#! U6 - https://doi.org/10.1016/j.mtcomm.2021.102428 SN - 2352-4928 VL - 27 ER - TY - GEN A1 - Fellah, Mamoun A1 - Hezil, Naouel A1 - Bouras, Dikra A1 - Montagne, Alex A1 - Obrosov, Aleksei A1 - Jamshed, Wasim A1 - Ibrahim, Rabha W. A1 - Iqbal, Amjad A1 - El Din, Sayed M. A1 - Khalifa, Hamiden Abd El-Wahed T1 - Investigating the effect of milling time on structural, mechanical and tribological properties of a nanostructured hiped alpha alumina for biomaterial applications T2 - Arabian Journal of Chemistry N2 - In this work was prepared α-Al2O3 alloys from laboratory aluminum oxide powder that was milled for different periods of time and sintered at a temperature of 1450 °C. The difference between the prepared samples was studied using several experimental measurement techniques, including X-ray diffraction, scanning electron microscopy and measurement of physical and mechanical properties. Moreover, the effect of milling time on the formation and sintering of alpha-alumina, by milling the mixture at different times using high energy crushing technique was studied. An influence of milling time on density, open spaces and microstructure of the samples was analyzed. The obtained results showed that longer milling duration led to alloys with higher hardness (H) and modulus of elasticity (E). This improvement is due to lower porosity and corresponding higher density at high temperatures. A noticeable decrease in the size of the particles with the increase of the milling time led to an increase in the lattice parameter accompanied by a decrease in defects and ionic voids. The percentage of pores reached 0.04 % within 24 h of grinding after it was approximately 0.20 %, while the density reached 96 % after the same highest grinding time. Tests showed that the value of friction coefficient decreases, while it increases with the increase in the applied pressure force and this was confirmed by SEM images of the samples. the main factor to reduce friction is the increase in grinding time, regardless of the value of the applied load. The results showed that the Al2O3 alloy applied to it with a load of 2 N and milled for 24 h had a minimum value of 1.94 µm3 wear volumes and a wear rate of 1.33 (µm3∙N−1∙µm−1). The sample milled for 24 h showed the best result, characterized by the lowest wear size, specific wear rate and the highest hardness with extraordinary density of 96 %, which is important in the field of biomaterials applications. KW - α-Al2O3 KW - Milling time KW - Nanomaterials KW - Particle size KW - Hardness KW - Biomaterials KW - Biomedical applications Y1 - 2023 UR - https://www.sciencedirect.com/science/article/pii/S1878535223005749 U6 - https://doi.org/10.1016/j.arabjc.2023.105112 SN - 1878-5379 VL - 16 IS - 10 ER -