TY - GEN A1 - Baigonakova, Gulsharat A1 - Marchenko, Ekaterina A1 - Chekalkin, Timofey A1 - Kang, Ji-hoon A1 - Weiß, Sabine A1 - Obrosov, Aleksei T1 - Influence of Silver Addition on Structure, Martensite Transformations and Mechanical Properties of TiNi–Ag Alloy Wires for Biomedical Application T2 - Materials N2 - The microstructural and functional behavior of TiNi-based wires with a silver content of 0–1.5 at.% was evaluated. The concentration range for Ag doping determined for the TiNi wires with potential for the medical industry was 0–0.2 at.%. Microstructure analysis of TiNi wires with different silver contents at room temperature indicated a multiphase structural state. Various internal structures with tangled grain boundaries were formed by intense plastic deformation. The nanocrystalline structure and phase state of wire with the minimum silver content (0.1 at.% Ag) provide full shape recovery, the greatest reversible strain, and optimal strength and ductility. TiNi ingots with a high Ag content (0.5–1.5 at.%) cracked under minimum load due to excess silver that crystallized along the grain boundaries and broke cohesion bonds between the TiNi grains. KW - shape memory alloy KW - silver KW - doping KW - mechanical properties KW - nanostructured material KW - wire Y1 - 2020 UR - https://www.mdpi.com/1996-1944/13/21/4721 U6 - https://doi.org/10.3390/ma13214721 SN - 1996-1944 VL - 13 IS - 21 ER - TY - GEN A1 - Morozova, Iuliia A1 - Obrosov, Aleksei A1 - Naumov, Anton A1 - Królicka, Aleksandra A1 - Golubev, Iurii A1 - Bokov, Dmitry O. A1 - Doynov, Nikolay A1 - Weiß, Sabine A1 - Michailov, Vesselin T1 - Impact of Impulses on Microstructural Evolution and Mechanical Performance of Al-Mg-Si Alloy Joined by Impulse Friction Stir Welding T2 - Materials N2 - Impulse Friction Stir Welding (IFSW) was utilized to join 6082–T6 alloy plates at various impulse frequencies. A distinctive feature of IFSW is the generation of mechanical impulses that enhances the forging action of the tool, and thereby, alters the weld microstructure. The microstructural evolution in the Stir Zone (SZ) with special focus on the strengthening precipitation behavior, and overall mechanical properties of the IFSW joints have been investigated. It was demonstrated that the strengthening β″ precipitates reprecipitated in the SZ of the IFSW joints during natural aging. In contrast, no precipitates were found in the SZ of the Friction Stir Welding (FSW) weld. Partial reversion of β″ after IFSW is supposed to occur due to more developed subgrain network and higher dislocation density introduced by impulses that accelerated precipitation kinetics. Dynamic recrystallisation was facilitated by impulses resulting in a fine, homogeneous structure. There was no significant difference between the microhardness in the SZ, tensile and yield strength of the FSW and IFSW joints. However, the application of impulses demonstrated the smoothing of the hardness reduction in the transition region at the advancing side. The shift of the fracture location from the Heat-Affected Zone (HAZ) by FSW to the SZ as well as higher elongation of the joints by IFSW of lower frequencies could be related to the grain refinement and the change of the grain orientation. KW - Al-Mg-Si alloy KW - impulse friction stir welding (IFSW) KW - precipitation KW - microstructure evolution KW - mechanical properties Y1 - 2021 UR - https://www.mdpi.com/1996-1944/14/2/347/htm U6 - https://doi.org/https://doi.org/10.3390/ma14020347 SN - 1996-1944 VL - 14 IS - 2 ER - TY - GEN A1 - Kashkarov, Egor B. A1 - Obrosov, Aleksei A1 - Sutygina, Alina A1 - Uludintceva, Elena A1 - Mitrofanov, Andrei A1 - Weiß, Sabine T1 - Hydrogen Permeation, and Mechanical and Tribological Behavior, of CrNx Coatings Deposited at Various Bias Voltages on IN718 by Direct Current Reactive Sputtering T2 - Coatings N2 - In the current work, the microstructure, hydrogen permeability, and properties of chromium nitride (CrNₓ) thin films deposited on the Inconel 718 superalloy using direct current reactive sputtering are investigated. The influence of the substrate bias voltage on the crystal structure, mechanical, and tribological properties before and after hydrogen exposure was studied. It was found that increasing the substrate bias voltage leads to densification of the coating. X-ray diffraction (XRD) results reveal a change from mixed fcc-CrN + hcp-Cr₂N to the approximately stoichiometric hcp-Cr₂N phase with increasing substrate bias confirmed by wavelength-dispersive X-ray spectroscopy (WDS). The texture coefficients of (113), (110), and (111) planes vary significantly with increasing substrate bias voltage. The hydrogen permeability was measured by gas-phase hydrogenation. The CrN coating deposited at 60 V with mixed c-CrN and (113) textured hcp-Cr₂N phases exhibits the lowest hydrogen absorption at 873 K. It is suggested that the crystal orientation is only one parameter influencing the permeation resistance of the CrNx coating together with the film structure, the presence of mixing phases, and the packing density of the structure. After hydrogenation, the hardness increased for all coatings, which could be related to the formation of a Cr₂O₃ oxide film on the surface, as well as the defect formation after hydrogen loading. Tribological tests reveal that hydrogenation leads to a decrease of the friction coefficient by up to 40%. The lowest value of 0.25 ± 0.02 was reached for the CrNₓ coating deposited at 60 V after hydrogenation. KW - CrNx coatings KW - Physical Vapour Deposition (PVD) KW - hydrogenation KW - tribology KW - mechanical properties KW - X-ray diffraction Y1 - 2018 UR - http://www.mdpi.com/2079-6412/8/2/66/htm U6 - https://doi.org/10.3390/coatings8020066 SN - 2079-6412 N1 - Special Issue "Surface Preparation and Treatments for Enhancing the Coating Performance" VL - 8 IS - 2 ER - TY - GEN A1 - Obrosov, Aleksei A1 - Sutygina, Alina A1 - Volinsky, Alex A. A1 - Manakhov, Anton A1 - Weiß, Sabine A1 - Kashkarov, Egor B. T1 - Effect of Hydrogen Exposure on Mechanical and Tribological Behavior of CrₓN Coatings Deposited at Different Pressures on IN718 T2 - Materials N2 - In the current study, the properties of the CrₓN coatings deposited on the Inconel 718 superalloy using direct current reactive magnetron sputtering are investigated. The influence of working pressure on the microstructure, mechanical, and tribological properties of the CrₓN coatings before and after high-temperature hydrogen exposure is studied. The cross-sectional scanning electron micrographs indicate the columnar structure of the coatings, which changes from dense and compact columns to large columns with increasing working pressure. The Cr/N ratio increases from 1.4 to 1.9 with increasing working pressure from 300 to 900 mPa, respectively. X-ray diffraction analysis reveals a change from mixed hcp-Cr₂N and fcc-CrN structure to approximately stoichiometric Cr₂N phase. After gas-phase hydrogenation, the coating deposited at 300 mPa exhibits the lowest hydrogen absorption at 600 °C of all investigated coatings. The results indicate that the dense mixed cubic and hexagonal structure is preferential for hydrogen permeation resistance due to the presence of cubic phase with higher packing density in comparison to the hexagonal structure. After hydrogenation, no changes in phase composition were observed; however, a small amount of hydrogen is accumulated in the coatings. An increase of coating hardness and elastic modulus was observed after hydrogen exposure. Tribological tests reveal that hydrogenation leads to a decrease of the friction coefficient up to 20%–30%. The best value of 0.25 was reached for hydrogen exposed CrₓN coating deposited at 300 mPa. KW - CrₓN coatings KW - PVD KW - hydrogenation KW - tribology KW - mechanical properties KW - GDOES Y1 - 2017 UR - http://www.mdpi.com/1996-1944/10/5/563/htm U6 - https://doi.org/10.3390/ma10050563 SN - 1996-1944 VL - 10 IS - 5 SP - 563 ER - TY - GEN A1 - Obrosov, Aleksei A1 - Naveed, Muhammad A1 - Volinsky, Alex A. A1 - Weiß, Sabine T1 - Substrate Frequency Effects on CrxN Coatings Deposited by DC Magnetron Sputtering T2 - Journal of Materials Engineering and Performance N2 - Controlled ion bombardment is a popular method to fabricate desirable coating structures and modify their properties. Substrate biasing at high frequencies is a possible technique, which allows higher ion density at the substrate compared with DC current bias. Moreover, high ion energy along with controlled adatom mobility would lead to improved coating growth. This paper focuses on a similar type of study, where effects of coating growth and properties of DC magnetron-sputtered chromium nitride (CrxN) coatings at various substrate bias frequencies are discussed. CrxN coatings were deposited by pulsed DC magnetron sputtering on Inconel 718 and (100) silicon substrates at 110, 160 and 280 kHz frequency at low duty cycle. Coating microstructure and morphology were studied by X-ray diffraction (XRD), atomic force microscopy (AFM), scanning electron microscopy (SEM), scratch adhesion testing and nanoindentation. Results indicate a transformation of columnar into glassy structure of CrxN coatings with the substrate bias frequency increase. This transformation is attributed to preferential formation of the Cr2N phase at high frequencies compared with CrN at low frequencies. Increase in frequency leads to an increase in deposition rate, which is believed to be due to increase in plasma ion density and energy of the incident adatoms. An increase in coating hardness along with decrease in elastic modulus was observed at high frequencies. Scratch tests show a slight increase in coating adhesion, whereas no clear increase in coating roughness can be found with the substrate bias frequency. KW - adhesion of coatings KW - CrN coatings KW - frequency KW - mechanical properties KW - microstructure KW - PVD KW - X-ray diffraction Y1 - 2016 UR - http://link.springer.com/article/10.1007/s11665-016-2426-4 U6 - https://doi.org/10.1007/s11665-016-2426-4 SN - 1544-1024 VL - 26 IS - 1 SP - 366 EP - 373 ER - TY - CHAP A1 - Obrosov, Aleksei A1 - Kashkarov, Egor B. A1 - Weiß, Sabine A1 - Volinsky, Alex A. ED - Tiwari, Ashutosh T1 - Mechanical and tribological behaviour of hydrogenated CrxN coatings deposited at different pressure and voltages on IN718 T2 - American Advanced Materials Congress 2016 N2 - Hydrogen degradation is a serious problem in industrial applications like power plants (boilers, turbines), marine structures, car and aircraft components, as it leads to failures as well as to deterioration of properties. Inconel 718 is one of the most commonly used materials for these applications. Different metal nitrides like TiN coatings have been deposited in past to prevent hydrogen degradation, which are also known for their high hardness and good wear resistance [1, 2]. However, reports on hydrogen degradation of CrN coatings, which shows better oxidation and corrosion resistance, higher temperature stability and lower friction coefficient than TiN [3, 4] has not been reported till now. Despite a lot of publications about CrN films, up to now the effect of hydrogenation on mechanical and tribological properties of CrN coatings is still not completely understood. In the current work CrxN coatings were deposited by Direct Current Magnetron Sputtering (dcMS) on Inconel 718 substrate at different chamber pressures and substrate voltages. Substrate voltage is one of the most important process parameters which determines the structure of the coating and the adhesion between substrate and coating. Simultaneously a study of the chamber pressure is also needed to understand the deposited structure and growth rate because at higher pressures the high number of argon atoms reduce the number of ionized ions available for the deposition leading to low deposition rates [5]. Gas-phase hydrogenation of the samples was performed at a temperature of 600° C and hydrogen pressure of 2 atm. It was found that CrxN coatings are resistant against hydrogen exposure as compared to uncoated surfaces. The results of changes in the mechanical, tribological properties and phase composition of the coatings after hydrogenation are discussed. Coating microstructure was studied by scanning electron microscopy (SEM). The mechanical properties of the coatings were characterized by means of nanoindentation and scratch test. KW - CrxN coating KW - mechanical properties KW - microstructure KW - hydrogenation KW - XRD Y1 - 2016 SN - 978-91-88252-03-6 PB - VBRI Press CY - Linköping ER -