TY - GEN A1 - Obrosov, Aleksei A1 - Gulyaev, Roman A1 - Ratzke, Markus A1 - Volinsky, Alex A. A1 - Bolz, Sebastian A1 - Naveed, Muhammad A1 - Weiß, Sabine T1 - XPS and AFM Investigations of Ti-Al-N Coatings Fabricated Using DC Magnetron Sputtering at Various Nitrogen Flow Rates and Deposition Temperatures T2 - Metals N2 - Ti-Al-N coatings were deposited by direct current magnetron sputtering (DCMS) onto IN 718 at different nitrogen flow rates and deposition temperatures. The coatings’ properties were characterized using atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS) as well as nanoindentation. It was found that higher deposition temperature leads to higher surface roughness and nitrogen flux influences the shape of grains. According to XPS, the bonding structure of all coatings exhibited the (Ti,Al)N phase. Mechanical properties depend on the Al content within the films. The coating with the best mechanical properties (deposited at 500 °C and 20 standard cubic centimeters per minute (sccm)) was further deposited onto tungsten carbide (WC) cutting tools for cylindrical turning experiments. A quasi-constant flank wear was observed until a machining volume of 23,500 mm³. KW - Ti-Al-N coatings KW - DC magnetron sputtering KW - XPS KW - AFM KW - nitrogen flow rate KW - surface morphology Y1 - 2017 UR - http://www.mdpi.com/2075-4701/7/2/52/htm U6 - https://doi.org/10.3390/met7020052 SN - 2075-4701 VL - 7 IS - 2 SP - 52 ER -