@misc{FroeschkeWolfHantuschetal., author = {Froeschke, Samuel and Wolf, Daniel and Hantusch, Martin and Giebeler, Lars and Wels, Martin and Gr{\"a}ßler, Nico and B{\"u}chner, Bernd and Schmidt, Peer and Hampel, Silke}, title = {Synthesis of micro- and nanosheets of CrCl3-RuCl3 solid solution by chemical vapour transport}, series = {Nanoscale}, volume = {29}, journal = {Nanoscale}, number = {14}, issn = {2040-3372}, doi = {10.1039/D2NR01366E}, pages = {10483 -- 10492}, abstract = {Solid solutions of 2D transition metal trihalides are rapidly growing in interest for the search for new 2D materials with novel properties at nanoscale dimensions. In this regard, we present a synthesis method for the Cr1-xRuxCl3 solid solution and describe the behaviour of the unit cell parameters over the whole composition range, which in general follows Vegard's law in the range of a = 5.958(6)CrCl3 … 5.9731(5)RuCl3 {\AA}, b = 10.3328(20)CrCl3 … 10.34606(21)RuCl3 {\AA}, c = 6.110(5)CrCl3 … 6.0385(5)RuCl3 {\AA} and β = 108.522(15)CrCl3 … 108.8314(14)RuCl3 °. The synthesized solid solution powder was subsequently used to deposit micro- and nanosheets directly on a substrate by applying chemical vapour transport in a temperature gradient of 575 °C → 525 °C for 2 h and 650 °C → 600 °C for 0.5 h as a bottom-up approach without the need for an external transport agent. The observed chromium chloride enrichment of the deposited crystals is predicted by thermodynamic simulation. The results allow for a nanostructure synthesis of this solid solution with a predictable composition down to about 30 nm in height and lateral size of several μm. When applying a quick consecutive delamination step, it is possible to obtain few- and monolayer structures, which could be used for further studies of downscaling effects for the CrCl3-RuCl3 solid solution. X-ray photoelectron spectroscopy, transmission electron microscopy and Raman spectroscopy were used to confirm the purity and quality of the synthesized crystals.}, language = {en} }