@misc{GawlińskaNęcekKotStarowiczetal., author = {Gawlińska-Nęcek, Katarzyna and Kot, Małgorzata and Starowicz, Zbigniew and Janusz-Skuza, Marta and Panek, Piotr and Marth, Ludwig and Plate, Paul and Flege, Jan Ingo}, title = {Reaction dynamics between formamidinium lead iodide and Copper Oxide}, series = {ACS Applied Materials \& Interfaces}, volume = {16}, journal = {ACS Applied Materials \& Interfaces}, number = {42}, publisher = {American Chemical Society (ACS)}, issn = {1944-8244}, doi = {10.1021/acsami.4c12990}, pages = {57878 -- 57887}, abstract = {Copper oxide (CuOx) has been announced as a very promising hole-transporting layer for perovskite solar cells. However, in our previous work, we have shown that once a formamidinium lead triiodide (FAPI) perovskite is spin-coated on a spray-coated cuprous oxide (Cu2O) substrate, the Cu2O diffuses into and reacts with the FAPI film. In order to verify if the degradation products are related to the oxidation state of CuOx and/or its preparation method, in this work, we first prepared CuOx films by thermal oxidation at temperatures ranging from 120 to 300 °C. While increasing the process temperature, a transformation from copper I (Cu2O) to copper II (CuO) oxidation states was observed. For both oxidation states of copper, FAPI perovskite degradation was found; however, some alterations in the reaction products were noticed. In contrast to our expectations, the introduction of an ultrathin plasma-enhanced atomic layer deposited Al2O3 layer in between both films only partially blocked the CuOx migration into the FAPI film. It can be concluded that regardless of the chemical composition and/or preparation method of CuOx, the overlayered FAPI film gets decomposed. In order to use CuOx as a hole-transporting layer in solar cells, new strategies must be developed to limit these unwanted chemical reactions.}, language = {en} } @misc{MerteBraudBussetal., author = {Merte, Lindsay R. and Braud, Nicolas and Buß, Lars and Bisbo, Malthe Kj{\ae}r and Wallander, Harald J. and Krisponeit, Jon-Olaf and Flege, Jan Ingo and Hammer, Bj{\o}rk and Falta, Jens and Lundgren, Edvin}, title = {Oxygen Storage by Tin Oxide Monolayers on Pt3Sn(111)}, series = {The Journal of Physical Chemistry. C}, volume = {127}, journal = {The Journal of Physical Chemistry. C}, number = {6}, issn = {1932-7447}, doi = {10.1021/acs.jpcc.2c09041}, pages = {2988 -- 2994}, abstract = {The high performance of platinum-tin catalysts for oxidation reactions has been linked to the formation of tin oxides at the metal surface, but little is known about the structure of these oxides or the chemical behavior that determines their catalytic properties. We show here how surface oxides on Pt3Sn(111) incorporate oxygen at the metal interface, which may be subsequently removed by reaction with CO. The storage mechanism, where oxygen uptake occurs without loss of interfacial Pt-Sn bonds, is enabled by the peculiar asymmetrical coordination state of Sn2+. O atoms are bound at pocket sites in the 2D oxide sheet between these outward-buckled Sn atoms and metallic Sn in the alloy surface below.}, language = {en} } @misc{ZuoMalekshahiByranvandKodalleetal., author = {Zuo, Weiwei and Malekshahi Byranvand, Mahdi and Kodalle, Tim and Zohdi, Mohammadreza and Lim, Jaekeun and Carlsen, Brian and Friedlmeier, Theresa Magorian and Kot, Małgorzata and Das, Chittaranjan and Flege, Jan Ingo and Zong, Wansheng and Abate, Antonio and Sutter-Fella, Carolin M. and Li, Meng and Saliba, Michael}, title = {Coordination Chemistry as a Universal Strategy for a Controlled Perovskite Crystallization}, series = {Advanced Materials}, volume = {35}, journal = {Advanced Materials}, number = {39}, issn = {0935-9648}, doi = {10.1002/adma.202302889}, abstract = {The most efficient and stable perovskite solar cells (PSCs) are made from a complex mixture of precursors. Typically, to then form a thin film, an extreme oversaturation of the perovskite precursor is initiated to trigger nucleation sites, e.g., by vacuum, an airstream, or a so-called antisolvent. Unfortunately, most oversaturation triggers do not expel the lingering (and highly coordinating) dimethyl sulfoxide (DMSO), which is used as a precursor solvent, from the thin films; this detrimentally affects long-term stability. In this work, (the green) dimethyl sulfide (DMS) is introduced as a novel nucleation trigger for perovskite films combining, uniquely, high coordination and high vapor pressure. This gives DMS a universal scope: DMS replaces other solvents by coordinating more strongly and removes itself once the film formation is finished. To demonstrate this novel coordination chemistry approach, MAPbI3 PSCs are processed, typically dissolved in hard-to-remove (and green) DMSO achieving 21.6\% efficiency, among the highest reported efficiencies for this system. To confirm the universality of the strategy, DMS is tested for FAPbI3 as another composition, which shows higher efficiency of 23.5\% compared to 20.9\% for a device fabricated with chlorobenzene. This work provides a universal strategy to control perovskite crystallization using coordination chemistry, heralding the revival of perovskite compositions with pure DMSO.}, language = {en} } @misc{BussBraudEwertetal., author = {Buß, Lars and Braud, Nicolas and Ewert, Moritz and Jugovac, Matteo and Mentes, Tevfik Onur and Locatelli, Andrea and Falta, Jens and Flege, Jan Ingo}, title = {In-situ growth characterization of 2D heterostructures: MoSe2 on intercalated graphene/Ru(0001)}, series = {Verhandlungen der DPG}, journal = {Verhandlungen der DPG}, publisher = {Deutsche Physikalische Gesellschaft}, address = {Bad Honnef}, issn = {0420-0195}, abstract = {Despite the great fundamental interest in 2D heterostructures, most of the investigated 2D heterostructures were realized by mechanical exfoliation or chemical vapor deposition in the millibar range, preventing true in-situ characterization of the growth process. Here, we have investigated the growth of MoSe2 on single-layer graphene on Ru(0001) via real-time in-situ low-energy electron microscopy and micro-diffraction. After preparation of the graphene by standard procedures from an ethylene precursor, MoSe2 has been prepared via co-deposition of Mo and Se. Prior Se intercalation of the graphene appears to enhance the subsequent growth of MoSe2 on the graphene. At elevated temperatures, rotational ordering of the MoSe2 is facilitated by the strongly enhanced mobility of single-domain MoSe2 islands that align with the high symmetry orientations of the underlying graphene, indicating a non-negligible interaction between the two van-der-Waals materials. Micro-spot angle-resolved photoemission proves the monolayer nature of the as-grown MoSe2 as well as the free-standing character of the Se-intercalated graphene underneath.}, language = {en} } @misc{KostoMoralesDevietal., author = {Kosto, Yuliia and Morales, Carlos and Devi, Anjana and Henkel, Karsten and Flege, Jan Ingo}, title = {Activity of cerium oxide thin films prepared by atomic layer deposition using custom and commercial precursors}, series = {Verhandlungen der DPG}, journal = {Verhandlungen der DPG}, publisher = {Deutsche Physikalische Gesellschaft}, address = {Bad Honnef}, issn = {0420-0195}, abstract = {Atomic layer deposition (ALD) allows preparation of conformal coatings with possibility to control their thickness at the submonolayer level, making it a good tool for depositing active layers on 3D structures. Our group is working on cerium oxide-based materials for hydrogen detection, which is difficult at ambient conditions due to the low sensitivity and long response time of the sensors. The cerium oxide layers prepared by ALD contain a lot of defects and provide an opportunity to overcome these complications. Thickness and morphology of the oxide films play an important role in defining the Ce3+/Ce4+ ratio, as well as the interface with the used substrate. Here, we compare cerium oxide thin films deposited by ALD techniques on SiO2 and Al2O3 substrates. The results reveal that the interface to the substrate can considerably influence the reactivity of the cerium oxide toward hydrogen and oxygen. Preparation of the oxides using two different precursors (commercial Ce(thd)4 and custom Ce(dpdmg)3) has been demonstrated to affect the redox properties of the films, their reactivity, and the reversibility.}, language = {en} } @misc{KotKediaPlateetal., author = {Kot, Małgorzata and Kedia, Mayank and Plate, Paul and Marth, Ludwig and Henkel, Karsten and Flege, Jan Ingo}, title = {Application of plasma enhanced atomic layer deposition process of alumina on perovskite film boosts efficiency of solar cells}, series = {Verhandlungen der DPG}, journal = {Verhandlungen der DPG}, publisher = {Deutsche Physikalische Gesellschaft}, address = {Bad Honnef}, issn = {0420-0195}, abstract = {It is assumed that plasma-enhanced atomic layer deposition (PEALD) cannot be used to prepare thin films on sensitive organic-inorganic perovskites because the plasma destroys the perovskite film and thus deteriorates its photophysical properties. Here, we prove that using an appropriate geometry of the ALD system (SENTECH SI PEALD system) and suitable process parameters it is possible to coat perovskites with alumina by PEALD. Spectromicroscopy followed by electrical characterisation reveal that as long as the PEALD process is not optimized (too long plasma pulses) one gets degradation of the perovskite as well as dissociation of the created iodine pentoxide (during PEALD) under light that causes a valence band maximum (VBM) shift to the Fermi level and thus significantly decreases the solar cell efficiency. However, once the PEALD process parameters are optimized, no VBM shift is observed. Moreover, the solar cell efficiency depends inversely on process temperature and layer thickness.}, language = {en} } @misc{MahmoodinezhadMoralesKotetal., author = {Mahmoodinezhad, Ali and Morales, Carlos and Kot, Małgorzata and Naumann, Franziska and Plate, Paul and Henkel, Karsten and Flege, Jan Ingo}, title = {A super-cycle approach to atomic layer deposition of indium-gallium-zinc oxide at low temperature}, series = {Verhandlungen der DPG}, journal = {Verhandlungen der DPG}, publisher = {Deutsche Physikalische Gesellschaft}, address = {Bad Honnef}, issn = {0420-0195}, abstract = {The continuing development of multifunctional devices needs novel multicomponent oxide layers, demanding a high control of both composition and thickness during their preparation. To this end, single metal oxides exhibiting high structural quality and conformity have successfully been grown by atomic layer deposition (ALD). However, the deposition of more complex compounds with specific optical and electrical properties is still challenging. In this work, we follow a bottom-up approach to design an ALD super-cycle to grow mixed indium-gallium-zinc oxide (IGZO) films with a controllable composition. For the formation of the individual indium, gallium, and zinc oxides, we found the use of plasma-enhanced ALD (PEALD) at 150 °C to be favorable when using the organometallic precursors trimethylindium, trimethylgallium, and diethylzinc together with oxygen plasma. The PEALD approach of IGZO films can particularly overcome a nucleation delay within the ZnO sub-cycle known from thermal ALD, achieving a higher growth per cycle and improving the quality and composition homogeneity of the films as shown by in-situ spectroscopic ellipsometry and ex-situ X-ray photoelectron spectroscopy.}, language = {en} } @misc{BraudBussLundgrenetal., author = {Braud, Nicolas and Buß, Lars and Lundgren, Edvin and Merte, Lindsay R. and Wallander, Harald J. and Krisponeit, Jon-Olaf and Locatelli, Andrea and Mentes, Tevfik Onur and Jugovac, Matteo and Flege, Jan Ingo and Falta, Jens}, title = {Cleaning and tailoring the Pt3Sn(111) surface for surface experiments}, series = {Surface Science}, volume = {732}, journal = {Surface Science}, issn = {0039-6028}, doi = {10.1016/j.susc.2023.122281}, abstract = {The cleaning process of the bimetallic Pt3Sn(111) surface has been studied by means of low-energy electron microscopy (LEEM), microspot low-energy electron diffraction (-LEED), and X-ray photoemission electron microscopy (XPEEM). Different cleaning procedures, performed under ultra-high vacuum conditions (UHV), including sputtering with argon ions and repeated cycles of annealing up to 1500 K were investigated. In this work, we show that a clean Pt3Sn(111) surface of high structural quality with a sharp and brilliant (2 × 2) bulk reconstruction in LEED as well as a perfectly smooth surface with terraces of micron size can be achieved by sputtering, annealing at very high temperatures, followed by a subsequent slow (0.09 K/s) and careful cooling procedure. Additionally, we show the possibility of tailoring the Sn concentration in the topmost layers of Pt3Sn(111) as a function of annealing temperature and subsequent cooling rate. Structural changes of the surface are induced by Sn segregation combined with a surface order-disorder transition at 1340 K. Moreover, two new surface reconstructions depending on the cooling rate are reported.}, language = {en} } @misc{MańkowskaMazurDomaradzkietal., author = {Mańkowska, Ewa and Mazur, Michał and Domaradzki, Jarosław and Mazur, Piotr and Kot, Małgorzata and Flege, Jan Ingo}, title = {Hydrogen Gas Sensing Properties of Mixed Copper-Titanium Oxide Thin Films}, series = {Sensors}, volume = {23}, journal = {Sensors}, number = {8}, issn = {1424-8220}, doi = {10.3390/s23083822}, abstract = {Hydrogen is an efficient source of clean and environmentally friendly energy. However, because it is explosive at concentrations higher than 4\%, safety issues are a great concern. As its applications are extended, the need for the production of reliable monitoring systems is urgent. In this work, mixed copper-titanium oxide ((CuTi)Ox) thin films with various copper concentrations (0-100 at.\%), deposited by magnetron sputtering and annealed at 473 K, were investigated as a prospective hydrogen gas sensing material. Scanning electron microscopy was applied to determine the morphology of the thin films. Their structure and chemical composition were investigated by X-ray diffraction and X-ray photoelectron spectroscopy, respectively. The prepared films were nanocrystalline mixtures of metallic copper, cuprous oxide, and titanium anatase in the bulk, whereas at the surface only cupric oxide was found. In comparison to the literature, the (CuTi)Ox thin films already showed a sensor response to hydrogen at a relatively low operating temperature of 473 K without using any extra catalyst. The best sensor response and sensitivity to hydrogen gas were found in the mixed copper-titanium oxides containing similar atomic concentrations of both metals, i.e., 41/59 and 56/44 of Cu/Ti. Most probably, this effect is related to their similar morphology and to the simultaneous presence of Cu and Cu2O crystals in these mixed oxide films. In particular, the studies of surface oxidation state revealed that it was the same for all annealed films and consisted only of CuO. However, in view of their crystalline structure, they consisted of Cu and Cu2O nanocrystals in the thin film volume.}, language = {en} } @misc{BakiAbdeldayemMoralesetal., author = {Baki, Aykut and Abdeldayem, Mohamed and Morales, Carlos and Flege, Jan Ingo and Klimm, Detlef and Bierwagen, Oliver and Schwarzkopf, Jutta}, title = {Potential of La-Doped SrTiO3 Thin Films Grown by Metal-Organic Vapor Phase Epitaxy for Thermoelectric Applications}, series = {Crystal Growth \& Design}, volume = {23}, journal = {Crystal Growth \& Design}, number = {4}, issn = {1528-7483}, doi = {10.1021/acs.cgd.2c01438}, pages = {2522 -- 2530}, abstract = {La-doped SrTiO3 thin films with high structural quality were homoepitaxially grown by the metal-organic vapor phase epitaxy (MOVPE) technique. Thermogravimetric characterization of the metal-organic precursors determines suitable flash evaporator temperatures for transferring the liquid source materials in the gas phase of the reactor chamber. An adjustment of the charge carrier concentration in the films, which is necessary for optimizing the thermoelectric power factor, was performed by introducing a defined amount of the metal-organic compound La(tmhd)3 and tetraglyme to the liquid precursor solution. X-ray diffraction and atomic force microscopy verified the occurrence of the pure perovskite phase exhibiting a high structural quality for all La concentrations. The electrical conductivity of the films obtained from Hall-effect measurements increases linearly with the La concentration in the gas phase, which is attributed to the incorporation of La3+ ions on the Sr2+ perovskite sites by substitution inferred from photoemission spectroscopy. The resulting structural defects were discussed concerning the formation of occasional Ruddlesden-Popper-like defects. The thermoelectric properties determined by Seebeck measurements demonstrate the high potential of SrTiO3 thin films grown by MOVPE for thermoelectric applications.}, language = {en} } @misc{MoralesKostoTschammeretal., author = {Morales, Carlos and Kosto, Yuliia and Tschammer, Rudi and Henkel, Karsten and Flege, Jan Ingo}, title = {Reduction by H2 exposure at room temperature of ceria ultrathin films grown by atomic layer deposition}, series = {Verhandlungen der DPG}, journal = {Verhandlungen der DPG}, publisher = {Deutsche Physikalische Gesellschaft}, address = {Bad Honnef}, issn = {0420-0195}, abstract = {Atomic layer deposition (ALD) exhibits a high potential for integration as a scalable process in microelectronics, allowing well-controlled layer-by-layer deposition and conformal growth on 3D structures. Yet, the ALD technique is also well known to lead to amorphous and defective, non-stoichiometric films, potentially resulting in modified materials properties that, in the case of ultra-thin deposits, can also be affected by film/substrate interaction. Interestingly, initial in situ X-ray photoemission spectroscopy (XPS) measurements of ceria ALD-deposits on Al2O3/Si, sapphire, and SiO2 substrates confirm a Ce3+/Ce4+ mixture dependent on the substrate interaction, deposit thickness, and morphology. Using near-ambient pressure XPS, we have significantly reduced ultrathin (< 10 nm) ceria films grown by ALD by exposing them to different O2/H2 partial pressures at moderate temperatures (< 525K). Notably, the total amount of reduction to Ce3+ is found to depend on the deposit thickness and initial ceria/substrate interaction. Furthermore, the intrinsic defects related to the ALD method seem to play a critical role in the reversible reduction at room temperature.}, language = {en} }