@incollection{FellahHezilAbderrahimetal., author = {Fellah, Mamoun and Hezil, Naouel and Abderrahim, Karima and Samad, Mohammed Abdul and Montagne, Alex and Mejias, Alberto and Iost, Alain and Kossman, Stephania and Chekalkin, Timofey and Obrosov, Aleksei and Weiß, Sabine}, title = {Investigating the Effect of Sintering Temperature on Structural and Tribological Properties of a Nanostructured Ti-20Nb-13Zr Alloy for Biomedical Applications}, series = {Characterization of Minerals, Metals, and Materials}, booktitle = {Characterization of Minerals, Metals, and Materials}, publisher = {Springer}, address = {Cham}, isbn = {978-3-030-36628-5}, issn = {2367-1181}, doi = {10.1007/978-3-030-36628-5_61}, pages = {619 -- 629}, abstract = {β-type Ti-20Nb-13Zr alloys with low Young's modulus were prepared at different sintering temperatures (950, 1050, 1150, and 1250 °C). The morphological and structural characteristics of as-prepared samples were investigated by several methods. Wear tests were conducted using a ball-on-plate type oscillating tribometer under different applied loads (2, 10, and 20 N). The morphological characterization indicated that the mean pore and crystallite size continuously decreased with increasing sintering temperature to reach lowest values of 40 nm and 38 nm at 1250 °C, respectively. The relative density of the 1250 °C sintered sample was as high as 98.7\%. Moreover, the higher sintering temperature resulted in higher relative density and closed porosity of the sample. Both the friction coefficient and wear rate were lower in the sample sintered at 1250 °C as compared to other samples. This enhancement in tribological properties was attributed to a closed porosity.}, language = {en} } @misc{FellahHezilTouhamietal., author = {Fellah, Mamoun and Hezil, Naouel and Touhami, Mohamed Zine and Hussien, Mohammed A. and Montagne, Alex and Mejias, Alberto and Iost, Alain and Kossman, Stephania and Chekalkin, Timofey and Obrosov, Aleksei and Weiß, Sabine}, title = {Effect of Sintering Temperature on Mechanical and Tribological Behavior of Ti-Ni Alloy for Biomedical Applications}, series = {TMS 2020 149th Annual Meeting \& Exhibition Supplemental Proceedings}, journal = {TMS 2020 149th Annual Meeting \& Exhibition Supplemental Proceedings}, publisher = {Springer}, address = {Cham}, isbn = {978-3-030-36295-9}, issn = {2367-1181}, doi = {10.1007/978-3-030-36296-6_157}, pages = {1701 -- 1710}, abstract = {Ti-Ni powder compacts were prepared by mechanical alloying (MA), followed by hot isostatic pressing (HIP). Afterwards, the samples were sintered at different temperatures (950, 1050, 1150 and 1250 °C). Microhardness, density, crystallite size as well as microstrain of the sintered samples were measured and analyzed. Wear characteristics in phosphate-buffered saline (PBS) solution was tested under different applied loads of 2 N, 10 N, and 20 N, respectively. The results indicated that the crystallite size continuously decreases with increasing sintering temperature and reaches the lowest value of 31.3 nm at 1250 °C. The relative density of the sample sintered at 1250 °C is 98.0\%. Moreover, the higher sintering temperatures lead to the higher relative density and the increase in hardness and young's modulus of the sample. At the same time the friction coefficient and wear rate were lower for the samples sintered at 1250 °C. This improvement in friction and wear resistance is attributed to the grain size refinement. Ti-Ni sintered at 1250 °C showed good tribological performance under all test conditions.}, language = {en} } @misc{HezilFellahMontagneetal., author = {Hezil, Naouel and Fellah, Mamoun and Montagne, Alex and Iost, Alain and Obrosov, Aleksei and Weiß, Sabine}, title = {Removal of Chromium (VI) from Water onto Activated Carbon by Adsorption in Dynamic Mode}, series = {TMS 2020 149th Annual Meeting \& Exhibition Supplemental Proceedings}, journal = {TMS 2020 149th Annual Meeting \& Exhibition Supplemental Proceedings}, publisher = {Springer}, address = {Cham}, isbn = {978-3-030-36295-9}, issn = {2367-1181}, doi = {https://doi.org/10.1007/978-3-030-36296-6_80}, pages = {855 -- 863}, abstract = {Hexavalent chromium pollution from industrial waste water is a serious problem as it can cause adverse effects on the environment. Several methods are used to reduce the harmful effects of this pollutant, especially physico-chemical methods, such as adsorption technology. The present study aims to remove Cr (VI) from industrial sources in a fixed-bed column of activated carbon. The experiments were carried out at natural pH and temperature with a flow rate (5, 10, and 20 mL/min) and bed height (3.5 cm). Breakthrough curves for feed concentrations (0.01, 0.03, and 0.05 mol/L) were investigated. The results indicated a marked decrease up to 99\%. The value of the flow constant for the Thomas model decreased with the increase in the concentration of the incoming substance, but increased with the increase in the flow rate.}, language = {en} } @misc{FellahHezilTouhamietal., author = {Fellah, Mamoun and Hezil, Naouel and Touhami, Mohamed Zine and Samad, Mohammed Abdul and Obrosov, Aleksei and Bokov, Dmitry O. and Marchenko, Ekaterina and Montagne, Alex and Iost, Alain and Alhussein, Akram}, title = {Structural, tribological and antibacterial properties of (α + β) based ti-alloys for biomedical applications}, series = {Journal of Materials Research and Technology}, volume = {9}, journal = {Journal of Materials Research and Technology}, number = {6}, issn = {2238-7854}, doi = {10.1016/j.jmrt.2020.09.118}, pages = {14061 -- 14074}, abstract = {Implant-related follow up complications resulting from poor implant integration, delamination, chipping, mechanical instability, inflammation or graft-vs-host reaction may lead to low patient tolerance, prolonged care and sometimes leading to a second surgery. Hence, there is an urgent need for developing biomaterials which will help to overcome the above compatibility problems. Ti based alloys have been widely used for biomedical applications, due to their excellent properties, such as low modulus, high biocompatibility and high corrosion resistance. In order to further improve the physical, mechanical and tribological properties of these alloys, microstructural modification is often required. Hence, this study aims to develop and evaluate the structural and tribological behavior of Hot Isostatic Pressed (HIPed) and sintered Ti-6Al-7Nb samples containing niobium, which is less toxic and less expensive as compared to the usual alloying element, vanadium (Ti-6Al-4 V). The Ti-6Al-7Nb alloys were fabricated by using nanoparticle powders milled for different durations (2, 6, 12 and 18 h) to evaluate the effect of milling time on the morphological and structural properties. Friction and wear tests were carried out on the (HIPed) and finally sintered Ti-6Al-7Nb alloy samples, to evaluate their tribological properties under different applied loads (2, 8 and 16 N), with an alumina α-Al2O3 ball as a counter face using an oscillating tribometer. The physical characterization of the nanopowders formed using different milling times indicated that the particle and crystallite size continually decreased with increasing milling time, while the microstrain increased. It is observed that the friction coefficient and wear rate for the samples prepared by powders milled for 18 h and tested under 2 N were lowest with values of 0.25 and 1.51 × 10-2 μm3∙N-1 μm-1, respectively compared to other milled samples. This improvement in tribological properties is attributed to the grain refinement at high milling times. The antibacterial evaluation of the fabricated alloys showed an improvement in antibacterial performance of the samples milled at 18 h compared to the other milling times.}, language = {en} } @misc{SaoudiFellahHeziletal., author = {Saoudi, Adel and Fellah, Mamoun and Hezil, Naouel and Lerari, Djahida and Khamouli, Farida and Atoui, L'hadi and Bachari, Khaldoun and Morozova, Iuliia and Obrosov, Aleksei and Samad, Mohammed Abdul}, title = {Prediction of mechanical properties of welded steel X70 pipeline using neural network modelling}, series = {International Journal of Pressure Vessels and Piping}, volume = {186}, journal = {International Journal of Pressure Vessels and Piping}, issn = {0308-0161}, doi = {10.1016/j.ijpvp.2020.104153}, pages = {8}, abstract = {An artificial neural network (ANN) model was developed to predict tensile and impact properties of a submerged arc helical welded (SAHW) pipeline steel API X70 based upon its chemical composition. Weight percent of the elements was considered as the input, while the tensile and Charpy impact properties were considered as the outputs. Scatter diagrams and two statistical parameters (absolute fraction of variance and relative error) were used to evaluate the prediction performance of the developed artificial neural network model. The predicted values were found to be in excellent agreement with the experimental data and the current model has a good learning precision and generalization (for training, validation and testing data sets). The results revealed that the developed model is very accurate and has a strong potential for capturing the interaction between the mechanical properties and chemical composition of welded high strength low alloy (HSLA) steels.}, language = {en} } @misc{FellahHezilGuerfietal., author = {Fellah, Mamoun and Hezil, Naouel and Guerfi, Kamel and Djellabi, Ridha and Montagne, Alex and Iost, Alain and Borodin, Kirill and Obrosov, Aleksei}, title = {Mechanistic pathways of cationic and anionic surfactants sorption by kaolinite in water}, series = {Environmental Science and Pollution Research}, volume = {28}, journal = {Environmental Science and Pollution Research}, number = {6}, issn = {1614-7499}, doi = {10.1007/s11356-020-11083-6}, pages = {7307 -- 7321}, abstract = {Surfactants are widely used in many chemical industries and as primary components of cleaning detergents due to their specific characteristics, which in turn results in high pollution of domestic and industrial wastewaters by such substances. In this study, the mechanistic pathways of the adsorption of cationic benzyl-dimethyl-dodecyl ammonium bromide (BDDAB) and anionic sodium dodecyl sulfate (SDS) surfactants on kaolinite clay in water were investigated. The results showed that the adsorption of anionic surfactant (SDS) on kaolinite is better compared with cationic surfactant (BDDAB), wherein the ♦maximum adsorption capacity was found 161.4 μmol g-1 and 234 μmol g-1 for BDDAB and SDS, respectively. Adsorption kinetics were the best suited to pseudo-second-order model for both BDDAB and SDS with an adsorption rate constant of 0.028 g μmol-1 min-1 and 0.023 g μmol-1 min-1, respectively. Meanwhile, the adsorption of BDDAB by kaolinite showed that the isotherm adsorption tended to follow the Langmuir-Freundlich and Freundlich isotherm models. However, the SDS adsorption isotherm obeyed only the Langmuir-Freundlich model.}, language = {en} } @misc{HazilFellahMontagneetal., author = {Hazil, Naouel and Fellah, Mamoun and Montagne, Alex and Iost, Alain and Obrosov, Aleksei and Weiß, Sabine}, title = {Study of the photocatalytic degradation of Orange methyl dye in the presence of titanium dioxide}, series = {La Troisi{\`e}me Conf{\´e}rence M{\´e}diterran{\´e}enne de la Biodiversit{\´e} 2019 (BIODIV 2019)}, journal = {La Troisi{\`e}me Conf{\´e}rence M{\´e}diterran{\´e}enne de la Biodiversit{\´e} 2019 (BIODIV 2019)}, publisher = {L'ASCOB-SYRTIS}, address = {Hammamet, Tunisie}, pages = {105}, abstract = {The use of photocatalytic techniques for water purification and wastewater treatment is very widespread, in our work we used TiO2 to photocatalyrate orange methyl (MO). In addition, the effects of some parameters on photodegradation of MO have been studied, such as the presence and / or absence of light (UV). The use of TiO2 showed a high MO degradation efficiency of up to 98\%. The presence of H2O2 in the photocatalytic reaction may favor the photocatalytic degradation efficiencies. In addition, the experimental results have demonstrated an excellent rate of the order of 99\%.}, language = {en} } @misc{FouziaFellahHeziletal., author = {Fouzia, Hammadi and Fellah, Mamoun and Hezil, Naouel and Aissani, Linda and Mimanne, Goussem and Mechachti, Said and Samad, Mohammed Abdul and Montagne, Alex and Iost, Alain and Weiß, Sabine and Obrosov, Aleksei}, title = {The effect of milling time on the microstructure and mechanical properties of Ti-6Al-4Fe alloys}, series = {Materials Today Communications}, volume = {27}, journal = {Materials Today Communications}, issn = {2352-4928}, doi = {10.1016/j.mtcomm.2021.102428}, pages = {11}, abstract = {Replacement of toxic and expensive vanadium (V) in medical grade titanium alloys with cheaper and non-toxic elements such as iron (Fe) or niobium (Nb), is an important step forward in developing safer and less expensive biomaterials. Evaluating the effect of different process parameters such as the milling time on the properties of these newly developed alloys helps in understanding and controlling their behavior. Hence, in this study, the influence of ball-milling duration (2, 6, 8, 12 and 18 h) on crystalline structure, phase evolution, densification, and mechanical characteristics of biomedical nanocrystalline Ti-6Al-4Fe (wt. \%) alloys is investigated. X-ray diffraction (XRD) confirmed that after 6 h of milling, aluminum (Al) and Fe completely dissolved into Ti matrix to form a solid solution of Ti (Al, Fe). XRD further revealed that the crystallite size decreased from 56 to 30 nm and the micro-strain increased with an increase in milling time. A decrease in porosity along with an increase in density is also observed for the alloys with increasing milling time. Moreover, the values of porosity obtained for the developed Ti-6Al-4Fe alloys ranged from 1 to 12 \%, which is comparable to the porosity of one of the cortical bones making it a potential candidate for bone replacements. Microhardness measurements showed that the hardness of the Ti-6Al-4Fe alloys was greater than the hardness of the conventional Ti-6Al-4V alloys. It was observed that the Ti-6Al-4Fe alloy fabricated with the powders milled for 2 h showed the lowest value of Young's Modulus. Milling time also had a significant effect on the surface roughness of the alloy samples, which showed a decreasing trend with increasing milling times.}, language = {en} } @misc{AissaniFellahChadlietal., author = {Aissani, Linda and Fellah, Mamoun and Chadli, Abdel Hakim and Samad, Mohammed Abdul and Cheriet, Abderrahmane and Salhi, Faiza and Nouveau, Corinne and Weiß, Sabine and Obrosov, Aleksei and Alhussein, Akram}, title = {Investigating the effect of nitrogen on the structural and tribo-mechanical behavior of vanadium nitride thin films deposited using R.F. magnetron sputtering}, series = {Journal of Materials Science}, volume = {56}, journal = {Journal of Materials Science}, number = {30}, issn = {1573-4803}, doi = {10.1007/s10853-021-06393-0}, pages = {17319 -- 17336}, abstract = {Magnetron sputtering is one of the most commonly used deposition techniques, which has received considerable attention in industrial applications. In particular, owing to its compatibility with conventional fabrication processes, it can produce and fabricate high-quality dense thin films of a wide range of materials. In the present study, nitrogen (N) was combined with pure vanadium in order to form binary nitride to improve its mechanical and tribological performance. To evaluate the influence of nitrogen on the structure of the as-deposited vanadium nitride (VN) coatings, the following techniques were used: XPS, XRD, SEM, AFM and optical profilometry. The residual stresses were determined by the curvature method using Stoney's formula. The hardness and Young's modulus were obtained by nanoindentation measurements. The friction behavior and wear characteristics of the films were evaluated by using a ball-on-disk tribometer. The obtained results showed that the N/V ratio increased with increasing the N2 flow rate while the deposition rate decreased. The preferred orientation was changed from (200) to (111) as the N2 flow rate increased with the presence of V-N and V-O binding energies as confirmed by XPS analysis. The nitrogen addition resulted in a columnar morphology and a fine structure with fine surface roughness. The VN thin film containing 49.5 at.\% of nitrogen showed the best performance: highest mechanical properties (hardness = 25 GPa), lowest friction coefficient (μ = 0.37) and lowest wear rate (Ws = 2.72 × 10-5 mm3N-1 m-1). A good correlation between the film microstructure, crystallite size, residual stress and mechanical and tribological properties was observed.}, language = {en} } @misc{AissaniFellahBelgrouneetal., author = {Aissani, Linda and Fellah, Mamoun and Belgroune, Ahlam and Obrosov, Aleksei and Samad, Mohammed Abdul and Alhussein, Akram}, title = {Effect of O2 flow rate on the structure, wettability and tribo-mechanical behaviour of Zr-O-N thin films}, series = {Surfaces and Interfaces}, volume = {26}, journal = {Surfaces and Interfaces}, issn = {2468-0230}, doi = {10.1016/j.surfin.2021.101441}, pages = {33}, abstract = {Structural and tribo-mechanical properties of Zr-O-N films deposited by reactive magnetron sputtering in a mixture of Ar (flow rate = 80 sccm), N2 (flow rate = 20 sccm) and O2 with a varying flow rate of 0 to 12 sccm were investigated. The films were characterized using scanning electron microscopy, energy dispersive x-ray analysis, atomic force microscopy, nanoindentation and wear tests. Oxygen content have a significant effect on the microstructure, wettability, tribo-mechanical properties of Zr-O-N films. The Zr-O-N films showed a dense structure with a mixture of zirconium oxides and nitrides and the preferred orientation changed from (111) ZrN to (200) ZrN with increasing O2 flow rate. The ZrON film, deposited at an oxygen flow rate of 10 sccm exhibited the highest contact angle (147°), the highest hardness (27.1 GPa), the lowest friction coefficient (0.36) and the lowest wear rate (5.8 × 10-7 mm3.Nm-1). The improvement in the tribological performance of the ZrON film deposited at 10 sccm is attributed to the improved hardness and increased H/E and H3/E2 ratios, due to the formation of a hard solid solution by the diffusion of oxygen.}, language = {en} }