@misc{ObrosovGulyaevRatzkeetal., author = {Obrosov, Aleksei and Gulyaev, Roman and Ratzke, Markus and Volinsky, Alex A. and Bolz, Sebastian and Naveed, Muhammad and Weiß, Sabine}, title = {XPS and AFM Investigations of Ti-Al-N Coatings Fabricated Using DC Magnetron Sputtering at Various Nitrogen Flow Rates and Deposition Temperatures}, series = {Metals}, volume = {7}, journal = {Metals}, number = {2}, issn = {2075-4701}, doi = {10.3390/met7020052}, pages = {52}, abstract = {Ti-Al-N coatings were deposited by direct current magnetron sputtering (DCMS) onto IN 718 at different nitrogen flow rates and deposition temperatures. The coatings' properties were characterized using atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS) as well as nanoindentation. It was found that higher deposition temperature leads to higher surface roughness and nitrogen flux influences the shape of grains. According to XPS, the bonding structure of all coatings exhibited the (Ti,Al)N phase. Mechanical properties depend on the Al content within the films. The coating with the best mechanical properties (deposited at 500 °C and 20 standard cubic centimeters per minute (sccm)) was further deposited onto tungsten carbide (WC) cutting tools for cylindrical turning experiments. A quasi-constant flank wear was observed until a machining volume of 23,500 mm³.}, language = {en} } @misc{ObrosovSutyginaManakhovetal., author = {Obrosov, Aleksei and Sutygina, Alina and Manakhov, Anton and Bolz, Sebastian and Weiß, Sabine and Kashkarov, Egor B.}, title = {Oxidation Behavior of Zr-1Nb Corroded in Air at 400 °C after Plasma Immersion Titanium Implantation}, series = {Metals}, volume = {8}, journal = {Metals}, number = {1}, issn = {2075-4701}, doi = {10.3390/met8010027}, pages = {16}, abstract = {In this paper, the influence of plasma immersion titanium implantation into the zirconium alloy Zr-1Nb on the oxidation behavior at 400 °C for 5, 24, 72, and 240 h in air under normal atmospheric pressure (101.3 kPa) was shown. The influence of implantation on the protective properties of the modified layer was shown. The valence of the oxides before and after implantation was analyzed by means of X-ray photoelectron spectroscopy (XPS). Grazing incidence X-ray diffraction (GIXRD) was carried out to examine the phase composition after titanium ion implantation and oxidation. Differential scanning calorimetry (DSC) revealed that titanium implantation exhibited effects of stabilizing the β phase. The formation of the t-ZrO2 and m-ZrO2 was observed during the oxidation of the as-received and modified Zr-1Nb. The measurement of weight gain showed an improvement in oxidation resistance of Ti implanted Zr-1Nb at the oxidation up to 24 h when compared with that of the as-received Zr-1Nb. However, at longer oxidation cycle the oxidation rate of Ti-implanted zirconium alloy is the same with the as-received alloy, which attributed to the layer thickness. Nevertheless, the corrosion of the Ti-implanted alloy is more uniform, while a local corrosion and cracks was detected on the surface of the as-received alloy.}, language = {en} }