@misc{EisentrautStendalBolzetal., author = {Eisentraut, Mark and Stendal, Johan Andreas and Bolz, Sebastian and Bambach, Markus and Weiß, Sabine}, title = {Applying a softening adapted acceleration to the hot deformation of TNM-B1}, series = {MRS Fall Meeting 2020}, journal = {MRS Fall Meeting 2020}, abstract = {Hot isostatically forged TiAl turbine blades made of TNM-B1 are commercially used in aircraft engines, as they offer significantly lower weight than the traditional nickel-based blades while exhibiting similar strength. Like other TiAl alloys, TNM-B1 displays high peak stress followed by a strong softening behavior (i.e. stress reduction) during hot deformation. This softening can be used to accelerate the deformation process by reducing the processing time and in turn the costs for TNM-B1 parts. In order to avoid increased damage during the accelerated process, a pre-heat treatment (HT) for the hot isostatically pressed material (HIP) is required. To simulate the accelerated forming process, hot compression tests were performed with a DIL805A/D/T dilatometer from TA Instruments (New Castle, Delaware, USA) with different strain rates (0.0013, 0.005, 0.01 and 0.05) and temperatures (T=1150, 1175 and 1200°C). Deformation of the heat-treated state revealed lower flow stress (in both, peak stresses and steady state stresses) and fewer voids compared to the HIP state (Fig. 1.a). The compression test data were used to develop material and temperature specific strain rate profiles based on a material model. Subsequently, hot compression tests were performed with different strain rate profiles (starting strain rates 0.0013 and 0.0052) for the HIP and the HT state. The results were evaluated with regard to their microstructure, deformation, and damage behavior. A reduction of the processing time for all tested strain rates profiles by factors 2-3 could be achieved compared to constant strain rates. Furthermore, the results indicated that the deformation with strain rate profiles (compared to constant strain rates) did not significantly change the resulting microstructure or damage tolerance of the HT state.}, language = {en} }