TY - GEN A1 - Froeschke, Samuel A1 - Wolf, Daniel A1 - Hantusch, Martin A1 - Giebeler, Lars A1 - Wels, Martin A1 - Gräßler, Nico A1 - Büchner, Bernd A1 - Schmidt, Peer A1 - Hampel, Silke T1 - Synthesis of micro- and nanosheets of CrCl3–RuCl3 solid solution by chemical vapour transport T2 - Nanoscale N2 - Solid solutions of 2D transition metal trihalides are rapidly growing in interest for the search for new 2D materials with novel properties at nanoscale dimensions. In this regard, we present a synthesis method for the Cr1−xRuxCl3 solid solution and describe the behaviour of the unit cell parameters over the whole composition range, which in general follows Vegard's law in the range of a = 5.958(6)CrCl3 … 5.9731(5)RuCl3 Å, b = 10.3328(20)CrCl3 … 10.34606(21)RuCl3 Å, c = 6.110(5)CrCl3 … 6.0385(5)RuCl3 Å and β = 108.522(15)CrCl3 … 108.8314(14)RuCl3 °. The synthesized solid solution powder was subsequently used to deposit micro- and nanosheets directly on a substrate by applying chemical vapour transport in a temperature gradient of 575 °C → 525 °C for 2 h and 650 °C → 600 °C for 0.5 h as a bottom-up approach without the need for an external transport agent. The observed chromium chloride enrichment of the deposited crystals is predicted by thermodynamic simulation. The results allow for a nanostructure synthesis of this solid solution with a predictable composition down to about 30 nm in height and lateral size of several μm. When applying a quick consecutive delamination step, it is possible to obtain few- and monolayer structures, which could be used for further studies of downscaling effects for the CrCl3–RuCl3 solid solution. X-ray photoelectron spectroscopy, transmission electron microscopy and Raman spectroscopy were used to confirm the purity and quality of the synthesized crystals. KW - Crystal growth KW - Chemical vapor transport KW - Thermal analysis KW - Thermodynamic modeling KW - 2D layered compounds Y1 - 2022 UR - https://opus4.kobv.de/opus4-UBICO/frontdoor/index/index/docId/29189 UR - https://pubs.rsc.org/en/content/articlelanding/2022/NR/D2NR01366E SN - 2040-3372 VL - 29 IS - 14 SP - 10483 EP - 10492 ER -