This thesis focuses on the investigation and characterization of the surfaces and interfaces of chalcopyrite-based Cu(In,Ga)Se₂ (CIGSe) and organo-metal mixed halide perovskites, specifically CH₃NH₃PbI(₃-ᵪ)Clᵪ thin film solar cell absorbers using various x-ray and electron spectroscopies. In particular, the impact of alkali treatments on the chemical and electronic surface and near-surface structure of CIGSe absorbers is studied. For CH₃NH₃PbI(₃-ᵪ)Clᵪ the compound formation is monitored and the peculiarities of the interface formation of CH₃NH₃PbI(₃-ᵪ)Clᵪ on compact and mesoporous TiO₂ are examined.
Laboratory and synchrotron-based photoelectron spectroscopy are used to gain a depth-dependent picture of the chemical and electronic structure in the surface and near-surface region of CIGSe absorbers, focusing on the influence of NaF and NaF/KF post-deposition treatments (PDT) when compared to alkali-free CIGSe absorbers. The alkali-free and NaF-PDT absorbers show similar chemical properties, having a Cu and Ga poor surface region compared to the nominal bulk and the same chemical environment for indium and selenium. For the NaF/KF-PDT samples a K-In-Se compound is present on top of a Cu-In-Ga-Se compound, with a nanopatterned surface that is almost devoid of Cu and Ga.
Further, for the NaF-PDT sample a near-surface electronic band gap of 1.61[+0.14/-0.51] eV is derived. In contrast, a large and more gradual change towards the surface is obtained for the NaF/KF-PDT absorber exhibiting a significant band gap widening of the surface, which is in agreement with a Cu- and Ga-devoid surface region and the formation of a K-In-Se surface compound.
To in-situ monitor the compound formation of CH₃NH₃PbI(₃-ᵪ)Clᵪ on compact TiO₂ (c-TiO₂) hard x-ray photoelectron spectroscopy is used. During in-situ annealing a drop-casted layer of precursor solution on c-TiO₂ shifts in the perovskite related core levels can be observed upon reach the “transition temperature” of 80-100°C. Further the Cl signal decrease at the onset of annealing and shows a depletion in the surface region for annealing temperatures above 50°C. In addition, the chemical and electronic structure of the interface between perovskite and mesoporous TiO₂ (mp-TiO₂) or c-TiO₂ using different perovskite layer thicknesses are studied.